对帘线钢中CaO-SiO2-Al2O3类夹杂物CaO与SiO2的比值和Al2O3含量进行了研究,并且通过热力学计算对CaO-SiO2-Al2O3系塑性夹杂物的生成条件进行了讨论.结果表明:生产帘线钢时,为了得到塑性良好的夹杂物,钢液的氧活度应控制在0.005 6～0.011 3,而酸溶铝含量应控制在0.000 10%～0.000 25%范围内.
参考文献
| [1] | 李一兵.对我国钢帘线发展问题的几点看法[A].天津:中国线材制品行业协会秘书处,2002:46-52. |
| [2] | 奥島敢.高清浄線材制造技術の進步[A].東京:日本铁鋼恊会,1985:147. |
| [3] | Bernard G;Ribound P V .Oxide Inclusions Plasticity[J].La Revue De Metallurgie-CIT,1981,78(05):421-433. |
| [4] | 陈家祥.炼钢常用图表数据手册[M].北京:冶金工业出版社,1998 |
| [5] | 日本學術振興會制鋼管19委員會.制鋼反応推獎平衡值(改訂増補)[M].,昭和59年:255. |
| [6] | Sigworth G K;Elliott J F .The Thermodynamics of Liquid Dilute Iron Alloys[J].Metal Science Journal,1974,18(03):298-310. |
| [7] | Howard M P;Bhattacharya D .Thermodynamics of Nozzle Blockage in Continuous Casting of Calcium-Containing Steels[J].Metallurgical and Materials Transactions,1984,15(03):547-562. |
| [8] | Gloria M F;Ramallugam S .Inclusion Precipitation Diagram for the Fe-O-Ca-Al System[J].Metallurgical and Materials Transactions,1980,11B(01):125-130. |
| [9] | 陈襄武.炼钢过程的脱氧[M].北京:冶金工业出版社,1991 |
| [10] | CHO S W;Suito H .Assessment of Calcium-Oxygen Equilibrium in Liquid Iron[J].ISIJ International,1994,34(03):265-269. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%