采用差热分析仪(DSC)、透射电子显微镜(TEM)等分析手段,研究应力/电场耦合时效后2524合金的DSC的曲线特征和微观组织.结果表明:与无外场时效(190℃/5 h)样品相比,施加25～130 MPa应力时效后,2524铝合金中S相析出体积分数升高,析出速率提高30％,S相的形成激活能降低55 kJ/mol;施加130 MPa+16 kV/cm耦合外场时效后,S相激活能仅降低了38 kJ/mol.
参考文献
| [1] | Hargarter H.;Starke EA.;Lyttle MT. .Effects of preferentially aligned precipitates on plastic anisotropy in Al-Cu-Mg-Ag and Al-Cu alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1):87-99. |
| [2] | 陈大钦,郑子樵,李世晨,陈志国,刘祖耀.外加应力对Al-Cu及Al-Cu-Mg-Ag合金析出相生长的影响[J].金属学报,2004(08):799-804. |
| [3] | 李剑,郑子樵,陈大钦,李世晨,殷顺高,刘祖耀.Al-Cu合金应力时效的动力学研究[J].稀有金属,2005(04):539-544. |
| [4] | Liu W.;Zheng YK.;Cui JZ.;Liang KM. .Study of the diffusion of Al-Li alloys subjected to an electric field[J].Journal of Materials Science,1998(4):1043-1047. |
| [5] | 魏齐龙,王永欣,陈铮.Al-Li合金相变的热分析动力学表征[J].稀有金属材料与工程,2006(06):941-944. |
| [6] | 潘峥嵘,郑子樵,李世晨,廖忠全.In对Al-3.5Cu合金析出过程的影响[J].稀有金属材料与工程,2011(06):1079-1083. |
| [7] | 栾佰峰,苏婧,黄天林,周军,张喜燕,刘庆.Sn含量对Zr-Sn-Nb-Fe-Cr合金相变温度和沉淀析出相的影响[J].稀有金属材料与工程,2012(05):830-834. |
| [8] | 周明哲,易丹青,贾延琳,刘阳平.预变形对2E12铝合金时效析出过程的影响[J].稀有金属材料与工程,2010(12):2107-2111. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%