Thermodynamic Aspects of Nanostructured CoAl Intermetallic Compound during Mechanical Alloying

材料科学技术（英文）, 2011, 27(7): 601-606.

Thermodynamic Aspects of Nanostructured CoAl Intermetallic Compound during Mechanical Alloying

^1, , ^2, , ^3, , ^4,

1.Department of Materials Engineering, Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, 84156-83111, Iran

2.Department of Materials Engineering, Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, 84156-83111, Iran

3.Department of Materials Engineering, Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, 84156-83111, Iran

4.Department of Materials Engineering, Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, 84156-83111, Iran

关键词：金属间化合物 , 机械合金化 , 热力学分析 , 煤炭生产 , 纳米结构 , 吉布斯自由能 , 最终产品 , 粉末混合物

Thermodynamic Aspects of Nanostructured CoAl Intermetallic Compound during Mechanical Alloying

Keywords： Intermetallics , CoAl , Nanostructured materials , Mechanical alloying , Thermodynamics ,

The nanostructured CoAl intermetallic compound was produced by mechanical alloying （MA） of the Co50Al50 elemental powder mixture in a planetary high energy ball mill. The ordered B2-CoAl structure with the grain size of about 6 nm was formed via a gradual reaction after 10 h of MA. A thermodynamic analysis of the process was also done. The results showed that the intermetallic compound of CoAl had the minimum Gibbs free energy compared to solid solution and amorphous states indicating the initial MA product was the most stable phase in the Co-Al system which was changed to a partially disordered structure with a steady long-range order of 0.82 at further milling. This amount of disordering caused the enthalpy of final product to show an increase of about 5.1 kJ·mol-1. Calculation of enthalpy related to the triple defect formation revealed that the enthalpy required for Al anti-sites formation was about 3 times greater than that for Co anti-sites formation.

参考文献

[1]	N.K. Mukhopadhyay;D. Mukherjee;S. Dutta .Synthesis and characterization of nanocrystalline and amorphous (Al_4Cu_9)_(94.5)Cr_(5.5) gamma-brass alloy by rapid solidification and mechanical milling[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2008(1/2):177-184.
[2]	P. Nandi;P.M.G. Nambissan;I. Manna .Amorphisation and intermetallic nanophase formation in ball-milled Al-Ti-Si studied through positron lifetime spectroscopy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):179-187.
[3]	C. Suryanarayana .Mechanical alloying and milling[J].Progress in materials science,2001(1/2):1-184.
[4]	A. A. Karimpoor;U. Erb;K. T. Aust;G. Palumbo .High strength nanocrystalline cobalt with high tensile ductility[J].Scripta materialia,2003(7):651-656.
[5]	T. Mousavi;F. Karimzadeh;M.H. Abbasi .Synthesis and characterization of nanocrystalline NiTi intermetallic by mechanical alloying[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):46-51.
[6]	R. A. Varin;T. Czujko;J. Mizera .Microstructural evolution during controlled ball milling of (Mg_2Ni + MgNi_2) intermetallic alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):332-339.
[7]	L.C. Zhang;K.B. Kim;P. Yu .Amorphization in mechanically alloyed (Ti, Zr, Nb)-(Cu, Ni)-Al equiatomic alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):157-163.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Thermodynamic Aspects of Nanostructured CoAl Intermetallic Compound during Mechanical Alloying

Thermodynamic Aspects of Nanostructured CoAl Intermetallic Compound during Mechanical Alloying

参考文献