Based on the variation of dislocation density, which is influenced by rolling variables in hot strip-rolling process, a yield stress model was constructed. An integrated model was built to predict the temperature variation and microstructure evolution, in which the Orowan formula was used to calculate the stress and strain, and the finite difference method was adopted to determine the temperature field. This model was applied to predict the temperature variation, austenite grain size and phase transformation in hot strip-rolling process, and the prediction results are in good agreement with the measured ones on 2 050 mm continuous hot strip-rolling mill.
参考文献
| [1] | Liu Zhen-yu;Han Shu-zhi;Wang Guo-dong et al.PredictingCalculation of Temperature Variation during Hot-Strip Rollingand Its Application[J].Iron and Steel,1994,29(02):31-34. |
| [2] | Yoshida H .A Coupling Analysis of Temperature, RollingLoads and Metallurgical Properties in Hot Strip Mills[J].Journal of the Japan Society for Technology of Plasticity,1997,38(06):577-581. |
| [3] | J. Yanagimoto;K. Karhausen;A. J. Brand;R. Kopp .Incremental formulation for the prediction of flow stress and microstructural change in hot forming[J].Journal of manufacturing science and engineering,1998(2):316-322. |
| [4] | Jun YANAGIMOTO;Jinshan LIU .Incremental Formulation for the Prediction of Microstructural Change in Multi-pass Hot Forming[J].ISIJ International,1999(2):171-175. |
| [5] | Liu Jin-shan;Yanagida A;Sugiyama S et al.Analysis ofPhase Transformation for Prediction of Microstructure Change after Hot Forming[J].ISIJ International,2001,41(12):1510-1516. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%