The effect of rare earths (RE) ranging from 0.1% to 1.2%(mass fraction) on hot cracking resistant property of Mg-Al alloys was investigated. The results show that hot cracking resistant property of Mg-Al alloys remarkably declines with an increase of RE addition. The causes of the decline are as follows: First, grain coarsening of Mg-Al alloys caused by RE addition reduces the fracture strain required for hot crack initiation. Second, RE reduces the eutectic microstructure of MgAl alloys, and as a result, shortens the time that the feeding channel remains open, making it difficult to feed the alloy.Furthermore, RE elevates the eutectic reaction temperature, which leads to the decrease in the strength of the interdendritic liquid film at the late stage of solidification. Third, when α-Mg dendrites form continuous skeletons, the interdendritic Al11 RE3 phase tends to block the feeding channels and increases the difficulty of feeding. Last, the shrinkage ratio discrepancy between Al11RE3 phases and α-Mg matrix is prone to cause shrinkage stress and promote hot crack initiation.
参考文献
| [1] | Mordike B L;Ebert T .Magnesium properties-applications-potential[J].Materials Science and Engineering A,2001,302:37. |
| [2] | Friedrich H;Schumann S .Research for a "new age of magnesium" in the automotive industry[J].Journal of Materials Processing Technology,2001,117:276. |
| [3] | Schumann S;Friedrich H.Current and future use of magnesium in the automobile industry[A].Switzerland:Trans.Tech.Publications Ltd,2003:419-422,51. |
| [4] | Kaneko T;Suzuki M.Automotive applications of magnesium alloys[A].Switzerland:Trans.Tech.Publications Ltd,2003:419-422,67. |
| [5] | Luo A A.Recent magnesium alloy development for automotive powertrain applications[A].Switzerland:Trans.Tech.Publications Ltd,2003:419-422,57. |
| [6] | Aghion E;Bronfin B;Eliezer D.The art of developing new magnesium alloys for high temperature applications[A].Switzerland:Trans.Tech.Publications Ltd,2003:419-422,407. |
| [7] | King J F.Development of practical high temperature magnesium casting alloys[A].Germany:Wiley-VCH,2000:14. |
| [8] | Anyanwu IA;Gokan Y;Suzuki A;Kamado S;Kojima Y;Takeda S;Ishida T .Effect of substituting cerium-rich mischmetal with lanthanum on high temperature properties of die-cast Mg-Zn-Al-Ca-RE alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):93-99. |
| [9] | Evangelista E;Gariboldi E;Lohne O et al.High-temperature behaviour of as die-cast and heat treated Mg-Al-Si AS21X magnesium alloy[J].Materials Science and Engineering A,2004,387-389:41. |
| [10] | Dahle A K;Lee Y C;Nave M D et al.Development of the as-cast microstructure in magnesium-aluminium alloys[J].Journal of Light Metals,2001,1:61. |
| [11] | Wang Y S;Sun B D;Wang Q D et al.An understanding of the hot tearing mechanism in AZ91 magnesium alloy[J].Materials Letters,2002,53:35. |
| [12] | Wang YS.;Wang QD.;Ma CJ.;Ding WJ.;Zhu YP. .Effects of Zn and RE additions on the solidification behavior of Mg-9Al magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):178-182. |
| [13] | Tang B;Li SS;Wang XS;Zeng DB;Wu R .An investigation on hot-crack mechanism of Ca addition into AZ91D alloy[J].Journal of Materials Science,2005(11):2931-2936. |
| [14] | Tang B;Li SS;Wang XS;Zeng DB;Wu R .Effect of Ca/Sr composite addition into AZ91D alloy on hot-crack mechanism[J].Scripta materialia,2005(9):1077-1082. |
| [15] | 郭旭涛,李培杰,曾大本,刘树勋.混合稀土去除再生镁合金中的夹杂[J].中国有色金属学报,2004(08):1295-1300. |
| [16] | Wang Q;Zeng X;Ding W;Zhu Y;Li Q;Lan J;Lu Y .Study on the fluidity of AZ91+xRE magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):109-115. |
| [17] | 祁庆琚,刘勇兵,杨晓红.Friction and Wear Characteristics of Mg-Al Alloy Containing Rare Earths[J].稀土学报(英文版),2003(02):157-162. |
| [18] | 黄晓锋,周宏,何镇明.Structure Analysis of Oxidation Film of Ignition-Inhibition AZ91D Ma gnesium Alloy Added with Cerium[J].稀土学报(英文版),2003(01):73-76. |
| [19] | D.G. Eskin;Suyitno;L. Katgerman .Mechanical properties in the semi-solid state and hot tearing of aluminium alloys[J].Progress in materials science,2004(issue 5):629-711. |
| [20] | Chojechi A;Telejko I;Bogacz T .Influence of chemical composition on the hot tearing formation of cast steel[J].Theoretical and Applied Fracture Mechanics,1997,27:99. |
| [21] | 郑伟超,李双寿,汤彬,曾大本.稀土对AZ31B变形镁合金组织和力学性能的影响[J].中国有色金属学报,2006(02):197-204. |
| [22] | Lahaie D J;Bouchard M .Physical modeling of the deformation mechanisns of semisolid bodies and a mechanical criterion for hot tearing[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,2001,32(08):697. |
| [23] | 张诗昌,魏伯康,蔡启舟,王立世.Effect of mischmetal and yttrium on microstructures and mechanical properties of Mg-Al alloy[J].中国有色金属学会会刊(英文版),2003(01):83-87. |
| [24] | Nave M D;Dahle A K;StJohn D H.The role of zinc in the eutectic solidification of magnesium-aluminium-zinc alloys[A].United States:The Minerals,Metals & Materials Society,2000:243. |
| [25] | Ding H;Fu H Z;Liu Z Y et al.Compensation of solidification contraction and hot cracking tendency of alloys[J].Acta Metallurgica Sinica,1997,33(09):921. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%