采用等通道转角挤压工艺（ECAP）细化了Al-26%Si合金中的组织,研究了该合金在不同温度下的冲击性能及断口形貌。结果表明：ECAP能有效细化该合金的晶粒,块状初晶硅尺寸明显减小且棱角钝化,针状共晶硅呈颗粒状弥散分布于基体中,300℃下挤压16道次后合金的室温（11℃）冲击功约为铸态的5倍;低温下,挤压16道次后合金的冲击性能随温度下降变化不大;当冲击温度由室温升高至100℃时,合金的冲击性能有所下降;铸态试样的断裂机制以脆性断裂为主,挤压后试样的断裂机制以韧性断裂为主。
Equal channel angular pressing（ECAP） technology was applied to Al-26%Si alloy for refining the microstructure,the impact property and fracture morphology of the alloy were studied at different temperatures.The results show that ECAP could effectively refine grains of the alloy,decrease block primary silicon size and passivate edges.Needle-like eutectic silicon in granylar form dispersed in matrix.Room temperature impact energy of the alloy was 5 times of that of as-cast sample after pressing for 16 passes at 300 ℃.At low temperature,impact property of the alloy changed little with the decrease of temperature after pressing for 16 passes.Impact property of the alloy decreased when impact temperature raised to 100 ℃ from room temperature.The fracture mechanism of as-cast and pressed samples was mainly brittle fracture and ductile fracture respectively.
参考文献
| [1] | 葛良琦,颜银标,蒋良,杨军.高硅铝合金中初晶硅形态控制研究进展[J].材料导报,2007(03):70-73. |
| [2] | ZHANG Henghua,DUAN Haiti,SHAO Guangjie,XU Luoping.Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P[J].稀有金属(英文版),2008(01):59-63. |
| [3] | 孙宝德,李克,王俊,周尧和.镧、钇稀土在过共晶铝硅合金中的作用[J].上海交通大学学报,1999(07):795-798. |
| [4] | Aibin Ma;Kazutaka Suzuki;Naobumi Saito;Yoshinori Nishida;Makoto Takagi;Ichinori Shigematsu;Hiroyuki Iwata .Impact toughness of an ingot hypereutectic Al-23 mass% Si alloy improved by rotary-die equal-channel angular pressing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):181-189. |
| [5] | JIANG Jing-hua,MA Ai-bin,N. SAITO,A. WATAZU,LIN Ping-hua,Y. NISHIDA.Effect of microstructures on superplasticity of Al-11%Si alloy[J].中国有色金属学会会刊（英文版）,2007(03):509-513. |
| [6] | Aibin Ma;Naobumi Saito;Makoto Takagi;Yoshinori Nishida;Hiroyuki Iwata;Kazutaka Suzuki;Ichinori Shigematsu;Akira Watazu .Effect of severe plastic deformation on tensile properties of a cast Al-11 mass% Si alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):70-76. |
| [7] | 刘扭参,刘忠侠.复合变质对Al-20Si合金冲击性能的影响[J].特种铸造及有色合金,2008(12):975-977. |
| [8] | 陈鼎,陈振华.铝合金在低温下的力学性能[J].宇航材料工艺,2000(04):1-7. |
| [9] | 刘瑛,张新明,李慧中,高慧,刘波,李惠杰.2519铝合金的低温拉伸力学性能[J].中南大学学报（自然科学版）,2006(04):641-645. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%