采用容量法研究了Mg-Gd-Y-Zr合金表面铈转化膜的耐蚀性能,通过正交试验获得在其表面制备铈转化膜的最佳条件:pH值为10.0,成膜时间为30 min,成膜促进剂的浓度为0.05 mol/L,成膜温度为25 ℃.其影响程度为pH值>成膜时间>成膜促进剂的浓度>成膜温度.比较了铈转化膜、铬酸盐转化膜及光板镁合金在3.5%NaCl溶液中的耐蚀行为.实验结果表明铈转化膜显著地提高了镁合金的耐腐蚀性能.
参考文献
| [1] | 肖阳,张新明,陈健美,蒋浩.Mg-9Gd-4Y-0.6Zr合金挤压T5态的高温组织与力学性能[J].中国有色金属学报,2006(04):709-714. |
| [2] | Guo Xingwu;Chang Jianwei;He Shangming et al.[J].Electrochi-mica Acta,2007,52:2570. |
| [3] | Winston A W;Reid J B .[J].Industrial and Engineering Chemistry,1935,27(11):1333. |
| [4] | Rudd A L;Breslin C B .[J].Corrosion Science,2000,42:275. |
| [5] | Bonora P L;Andrei M .[J].Corrosion Science,2002,44:729. |
| [6] | Dabala M.;Brunelli K.;Napolitani E.;Magrini M. .Cerium-based chemical conversion coating on AZ63 magnesium alloy[J].Surface & Coatings Technology,2003(2/3):227-232. |
| [7] | Yi Jianlong;Zhang Xinming .[J].Scripta Materialia,2008,59:955. |
| [8] | Lindstrom R;Johansson L .[J].Corrosion Science,2004,46:1141. |
| [9] | Xuan Lin .An Environmentally Compliant Cerium-Based Conversion Coating for Aluminum Protection[D].Missouri:University of Missouri-Rolla,1998. |
| [10] | Ardelean H;Fiaud C .[J].Materials and Corrosion,2001,52:889. |
| [11] | Brunelli K;Dabala M .[J].Corrosion Science,2005,47:989. |
| [12] | Montemor, MF;Simoes, AM;Ferreira, MGS;Carmezim, MJ .Composition and corrosion resistance of cerium conversion films on the AZ31 magnesium alloy and its relation to the salt anion[J].Applied Surface Science,2008(6):1806-1814. |
| [13] | Katya Brunelli;Manuele Dabala;Irene Calliari et al.[J].Corrosion Science,2005,47:989. |
| [14] | Lindstrom Rakel;Johansson Lars Gunnar;Thompson George E et al.[J].Corrosion Science,2004,46:1141. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%