介绍了负载不同晶型TiO2薄膜电极的制备,并研究了聚乙二醇加入量、活化条件等对不同晶型、不同形貌、不同粒径纳米TiO2薄膜电极的光电催化活性的影响.结果表明:聚乙二醇加入量有一最佳值;且纳米级锐钛矿型TiO2和金红石型TiO2分别经600℃和400℃煅烧后,光电催化性能最好;粒径越小催化活性越高.当粒径小于25 nm时,可显示出量子尺寸效应.
参考文献
| [1] | 周学双 .[J].化工环保,1992,12(06):333-336. |
| [2] | 王怡中;胡春;汤鸿霄 .[J].环境科学学报,1995,15(04):472-479. |
| [3] | Zeltner W A;Hill C G;Anderson M A .Supported Titania for Photodegradation[J].CHEMTECH,1993,23(05):21-28. |
| [4] | Gerischer H;Heller A .[J].Journal of the Electrochemical Society,1992,139(01):113-118. |
| [5] | Wang C M;Heller A;Gerischer H .[J].Journal of the American Chemical Society,1992,114(13):5230. |
| [6] | Kato K.;Torii Y.;Taoda H.;Kato T.;Butsugan Y.;Tsuzuki A. .MORPHOLOGY OF THIN ANATASE COATINGS PREPARED FROM ALKOXIDE SOLUTIONS CONTAINING ORGANIC POLYMER, AFFECTING THE PHOTOCATALYTIC DECOMPOSITION OF AQUEOUS ACETIC ACID[J].Journal of Materials Science,1995(3):837-841. |
| [7] | 余家国,赵修建,陈文梅,任建军.太阳光TiO2多孔纳米薄膜光催化降解有机磷农药的研究[J].太阳能学报,2000(02):165-170. |
| [8] | Ohtani B;Zhang S;Hanada J .[J].Journal of Photochemistry and Photobiology A:Chemistry,1992,64:223-230. |
| [9] | 余锡宾,王桂华,罗衍庆,李和兴.二氧化钛纳米微粒的制备与光催化活性[J].化学研究与应用,2000(01):14-19. |
| [10] | 陶跃武;赵梦月;陈士夫 等.[J].催化学报,1997,18(04):345-347. |
| [11] | Kobata A;Kusakabe K;Morooka S .[J].AICHE Journal,1991,37(03):347-359. |
| [12] | Bickley R I;Lees J S et al.[J].Journal of Solid State Chemistry,1991,92:178-180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%