Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States

材料科学技术（英文）, 2014, 30(12): 1181-1192.

Zhiming Zhang ^1, , Jianqiu Wang ^2, , En-Hou Han ^3, , Wei Ke ^4,

1.Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

2.Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

3.Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

4.Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

基金项目: This work is supported by the Special Funds for the National Basic Research Program of China (No.2011CB610502),the National Science and Technology Major Project (No.2011ZX06004-009) and the National Natural Science Foundation of China (No.51025104).

Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States

Keywords： Alloy 690TT

参考文献

[1]	F. Scenini;R.C. Newman;R.A. Cottis .Effect of Surface Preparation on Intergranular Stress Corrosion Cracking of Alloy 600 in Hydrogenated Steam[J].Corrosion: The Journal of Science and Engineering,2008(11):824-835.
[2]	M. F. Montemor;M. G. S. Ferreira;M. Walls .Influence of pH on Properties of Oxide Films Formed on Type 316L Stainless Steel, Alloy 600, and Alloy 690 in High-Temperature Aqueous Environments[J].Corrosion: The Journal of Science and Engineering,2003(1):11-21.
[3]	P. Kritzer;N. Boukis .Review of the Corrosion of Nickel-Based Alloys and Stainless Steels in Strongly Oxidizing Pressurized High-Temperature Solutions at Subcritical and Supercritical Temperatures[J].Corrosion: The Journal of Science and Engineering,2000(11):1093-1104.
[4]	Y. -J. Kim .Analysis of oxide film formed on type 304 stainless steel in 288℃ water containing oxygen, hydrogen, and hydrogen peroxide[J].Corrosion: The Journal of Science and Engineering,1999(1):81-88.
[5]	Y.-J. Kim .Characterization of the Oxide Film Formed on Type 316 Stainless Steel in 288 deg C Water in Cyclic Normal and Hydrogen Water Chemistries[J].Corrosion: The Journal of Science and Engineering,1995(11):849-860.
[6]	C.S. Kumai;T.M. Devine .Oxidation of Iron in 288 deg C, Oxygen-Containing Water[J].Corrosion: The Journal of Science and Engineering,2005(3):201-218.
[7]	C.S. Kumai;T.M. Devine .Influence of Oxygen Concentration of 288 deg C Water and Alloy Composition on the Films Formed on Fe-Ni-Cr Alloys[J].Corrosion: The Journal of Science and Engineering,2007(12):1101-1113.
[8]	L. Tan;X. Ren;K. Sridharan;T.R. Allen .Effect of shot-peening on the oxidation of alloy 800H exposed to supercritical water and cyclic oxidation[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(7):2040-2046.
[9]	R. Fujisawa;K. Nishimura;T. Nishida .Corrosion Behavior of Nickel-Based Alloys and Type 316 Stainless Steel in Slightly Oxidizing or Reducing Supercritical Water[J].Corrosion: The Journal of Science and Engineering,2006(3):270-274.
[10]	F. Huang,J.Q. Wang,E.H. Han,W. Ke.Short-time Oxidation of Alloy 690 in High-temperature and High-pressure Steam and Water[J].材料科学技术学报：英文版,2012(06):562-568.
[11]	A.A. Hermas .XPS analysis of the passive film formed on austenitic stainless steel coated with conductive polymer[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(9):2498-2505.
[12]	A. Machet;A. Galtayries;S. Zanna;L. Klein;V. Maurice;P. Jolivet;M. Foucault;P. Combrade;P. Scott;P. Marcus .XPS and STM study of the growth and structure of passive films in high temperature water on a nickel-base alloy[J].Electrochimica Acta,2004(22/23):3957-3964.
[13]	J.B. Ferguson;Hugo F. Lopez .Oxidation Products of INCONEL Alloys 600 and 690 in Pressurized Water Reactor Environments and Their Role in Intergranular Stress Corrosion Cracking[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2006(8):2471-2480.
[14]	G. S. Was;S. Teysseyre;Z. Jiao .Corrosion of Austenitic Alloys in Supercritical Water[J].Corrosion: The Journal of Science and Engineering,2006(11):989-1005.
[15]	M. Bojinov;P. Kinnunen;G. Sundholm .Electrochemical Behavior of Nickel-Chromium Alloys in a High-Temperature Aqueous Electrolyte[J].Corrosion: The Journal of Science and Engineering,2003(2):91-103.
[16]	N. Bertrand;C. Desgranges;D. Poquillon .Iron Oxidation at Low Temperature (260-500 °C) in Air and the Effect of Water Vapor[J].Oxidation of Metals,2010(1/2):139-162.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
Zhiming Zhang Jianqiu Wang En-Hou Han Wei Ke
在百度学术搜索
Zhiming Zhang Jianqiu Wang En-Hou Han Wei Ke
在万方数据库搜索
Zhiming Zhang Jianqiu Wang En-Hou Han Wei Ke
在CNKI搜索
Zhiming Zhang Jianqiu Wang En-Hou Han Wei Ke

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States

参考文献