采用阳极氧化法在7050铝合金表面制备了两种厚度的氧化铝薄膜，再用搅拌摩擦焊对铝合金进行焊接，研究了表面氧化膜厚度对焊接接头性能的影响。结果表明，氧化膜厚度对焊接接头性能的影响与焊接参数密切相关，当氧化膜厚度为12．7μm，焊速为50mm·min^-1，搅拌针转速为600-800r·min^-1时，接头的抗拉强度十分接近表面为自然状态接头的，而当氧化膜厚度为44μm时，接头焊缝氧化物含量增多，接头强度与自然状态接头的强度相比大幅降低；氧化膜提高了焊核区的硬度，膜厚度为44um时焊核区硬度最高达265HV，最低约180HV．
The anodic oxidation method was adopted to prepare alumina film with two sorts of thickness on the surface of 7050 aluminum alloy, and then to weld by friction stir welding. The effect of surface oxidation film thickness on property of welded joints was studied. The results show that the effect of surface oxidation film thickness on property of welded joints was closely related to the welding parameters. When the thickness of oxidation film was 12.7μm, welded speed was 50 mm · min^-1 and the rotation rate of stirring pin was 600-800 r · min^-1 , the tensile strength of joints was close to the joint of natural state surface. But when the thickness of oxidation film was 44μm, the oxide content in weld seam raised and the tensile strength decreased prominently. The surface oxidation film increased the hardness of the welded core zone, the highest and lowest hardness value was 265 HV and 180 HV respectively when the film thickness was 44μm.
参考文献
| [1] | 陈继强,尹志民,何振波,彭勇宜.铝锌镁钪锆合金搅拌摩擦焊接头组织与性能[J].焊接学报,2009(10):68-72. |
| [2] | K.M. Feng;C.H. Pan;G.S. Zhang;D.L. Luo;Z.W. Zhou;Y.W. Yang;X.Y. Wang;G. Hu;T. Yuan;Z. Chen;H.Y. Wang;C.A. Chen;Z.X.Li;Z.Zhao;Z.Q. Li .Preliminary design for a China ITER test blanket module[J].Fusion engineering and design,2006(8/14):1219-1224. |
| [3] | Yutaka S. Sato;Fumie Yamashita;yusuke Sugiura;Seung Hwan C. Park;Hiroyuki Kokawa .FIB-assisted TEM study of an oxide array in the root of a friction stir welded aluminum alloy[J].Scripta materialia,2004(3):365-369. |
| [4] | C. Hamilton;S. Dymek;A. Sommers .A thermal model of friction stir welding in aluminum alloys[J].International Journal of Machine Tools & Manufacture: Design, research and application,2008(10):1120-1130. |
| [5] | Sato YS;Takauchi H;Park SHC;Kokawa H .Characteristics of the kissing-bond in friction stir welded Al alloy 1050[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):333-338. |
| [6] | 任淑荣,马宗义,陈礼清,张玉政.焊后热处理工艺和背部二次焊接对搅拌摩擦焊接7075-T651铝合金性能的影响[J].金属学报,2007(03):225-230. |
| [7] | Di SS;Yang XQ;Fang DP;Luan GH .The influence of zigzag-curve defect on the fatigue properties of friction stir welds in 7075-T6 Al alloy[J].Materials Chemistry and Physics,2007(2/3):244-248. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%