综述了化学细化技术的发展现状,并重点评述了该方法在高温合金领域的最新发展.指出利用以高熔点金属化合物为基本添加剂的细化方法是对高温合金一类复杂合金进行细化的有效手段,强调了进行形核细化机理研究的迫切性.
参考文献
| [1] | Sims C T.The Superalloys I[M].New York:Wiley,1972:15. |
| [2] | Sims C T.The Superalloys Ⅱ[M].New York:Wiley,1987:118. |
| [3] | 弗莱明斯M C.凝固过程[M].北京:冶金工业出版社,1985:311. |
| [4] | Glicksman M E;Childs W J .[J].Acta Materialia,1962,10:92. |
| [5] | Southin R T;Chadwick G A .[J].Scripta Metallurgica et Materialia,1969,3:541. |
| [6] | Crosley P B;Mondolfo L F .[Z].TMS,1971. |
| [7] | Mondolfo I F .Grain Refinement in Casting and Welds[Z].Warrendale,Pennsylvannia,AIME,1983. |
| [8] | Wood J V .Solidification and Casting of Metals[Z].TMS,1979. |
| [9] | 陈茂涛.催化作用原理[M].西安:西北大学出版社,1992:125. |
| [10] | Arnberg L;Bckerud L;Klang H.[J].Met Tech Jan,1982 |
| [11] | 李勇 .化学细化及动力学方法控制凝固组织的研究[D].西北工业大学,1998. |
| [12] | 刘林,张蓉,甄宝林.镍基高温合金铸件的晶粒组织控制--添加剂的影响[J].航空学报,1995(03):315. |
| [13] | Wanqi J;Rrif W .[J].Zeitschrift fur Metallkunde,1993,84:445. |
| [14] | Banerji A;Feng Q;Reif W .[J].Met,1987,41:1237. |
| [15] | 刘林.镍基高温合金铸件的晶粒组织控制铸造工艺参数的影响[J].航空学报,1994(11):1357. |
| [16] | 郑建邦 .K4169高温合金铸态晶粒细化的研究[D].西北工业大学,1996. |
| [17] | 张焕修.[J].铸工,1985(47):23. |
| [18] | 张焕修.[J].铸工,1985(51):1. |
| [19] | Jie Wanqi;Reif W.Proceedings of China-Janpan International Conference on Foundry Engineering[C].,1994:311. |
| [20] | Denzine A.[A].,1982:325. |
| [21] | Banerji A;Rrif W et al.[J].Searcher-The Magazine For Database Professionals,1991,1:4. |
| [22] | Dennison J P;Abbaschian G J;David S A .Grain Refinement in Casting and Welds[Z].The Metall Society of AIME,1983. |
| [23] | Lin L;Zhang R;Wang L.AMPT' 95 Conference[C].Dublin,1995:1329. |
| [24] | 郑建邦 等.[J].金属学报,1998,34(04):362. |
| [25] | 郭益平 .K3铸造高温合金晶粒细化及性能研究[D].西北工业大学,1998. |
| [26] | Freeman W;Sims C fretal.Superalloys- High Temperature Materials for Aerospace and Industrial Power[M].John White & Sons,Inc,1987:435. |
| [27] | Bain K;Gambone M;Hyzak J;Reichman S et al.Superalloys 1988[Z].The Metallurgical Society,1988. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%