对纳米羟基磷灰石(HA)进行KH570硅烷偶联剂化学改性处理后,采用溶液热共混方法制备KH570改性的HA/聚己内酯(PCL)复合材料.材料表征和检测结果表明:改性处理能使KH570硅烷偶联剂与n-HA发生化学反应连接,使复合材料的熔融温度升高0.2℃、结晶温度升高4.3℃.改性后HA在HA/PCL复合材料中呈现较均匀分布,使材料力学强度升高了3.93MPa,杨氏模量提高了263.63 MPa.KH570改性有效地提高了HA/PCL复合材料的力学性能.
参考文献
[1] | Chang, KY;Lin, CC;Ho, GH;Huang, YP;Lee, YD .Synthesis and self-assembly of comb-like amphiphilic Doxifluridine-poly(epsilon-caprolactone)-graft-poly(gamma-glutamic acid) copolymer[J].Polymer: The International Journal for the Science and Technology of Polymers,2009(7):1755-1763. |
[2] | Wei X W;Gong C Y;Shi S et al.Self-assembled honokiol-loaded micelles based on poly(ε-caprolactone)-poly(ethylene glyc01)-poly(ε-capmlactone)copolymet[J].International Journal of Pharmaceutics,2009,369:170-175. |
[3] | Lee B T;Quang D V;Youn M H et al.Fabrication of biphasic calcium phosphates/polycapmlactone composites by melt infiltration process[J].J Mater Sei Mater Med,2008,19(05):2223-2229. |
[4] | Chen BQ;Sun K .Mechanical and dynamic viscoelastic properties of hydroxyapatite reinforced poly(epsilon-caprolactone)[J].Polymer Testing,2005(8):978-982. |
[5] | Chen BQ;Sun K .Poly (epsilon-caprolactone)/hydroxyapatite composites: effects of particle size, molecular weight distribution and irradiation on interfacial interaction and properties[J].Polymer Testing,2005(1):64-70. |
[6] | Wong, SC;Baji, A .Fracture strength and adhesive strength of hydroxyapatite-filled polycaprolactone[J].Journal of Materials Science. Materials in Medicine,2008(2):929-936. |
[7] | Neumann M;Epple M .Composites of calcium phosphate and polymers as bone substitution materials[J].European journal of trauma,2006(2):125-131. |
[8] | Tanaka H;Watanabe T;Chikasawa M et al.TPD,FTIR and molecular adsorption studies of calcium hydroxyapatite surface modified with hexanoic and decanoic acids[J].Journal of Colloid and Interface Science,1999,214(01):31-37. |
[9] | Tanaka H.;Chikazawa M.;Kandori K.;Ishikawa T.;Watanabe T. .Surface structure and properties of calcium hydroxyapatite modified by hexamethyldisilazane[J].Journal of Colloid and Interface Science,1998(1):205-211. |
[10] | J. Lannutti;J. Luo;R. Seghi .Effect of silane coupling agents on the wear resistance of polymer-nanoporous silica gel dental composites[J].Materials science & engineering, C. Biomimetic and supramolecular systems,1997(1):15-22. |
[11] | 廖建国,王学江,左奕,张利,文季秋,李玉宝.硅烷偶联剂对纳米羟基磷灰石表面改性的研究[J].无机材料学报,2008(01):145-149. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%