In order to overcome the limitations of low adhesion strength and poor thermal-shock resistance of pure ceramic coatings, Cu-Al2O3 gradient coatings were fabricated by plasma spraying. The microstructure and distribution of Cu-Al2O3 gradient coatings were analyzed. The adhesion strength, thermal-shock resistance and porosity of the coatings were tested. The results show that the composition of the gradient coatings has a gradient distribution along the thickness of coatings. As copper has a relatively low melting point and the molten copper has good wettability on the surface of Al2O3, it can be melted sufficiently and could fill the interstices and pores among the spraying particles effectively, thus improves the adhesion strength, thermal shock resistance and reduces the porosity. The adhesion strength of the gradient coating is 15.2 MPa which is two times of that of the double-layer structure coating.
参考文献
| [1] | L. Dumitrescu;F. Maury .Al{sub}2O{sub}3 coatings on stainless steel from Al metal-organic chemical vapor deposition and thermal treatments[J].Surface & Coatings Technology,2000(1/3):419-423. |
| [2] | L. H. Cao;K. A. Khor;L. Fu;F. Boey .Plasma spray processing of Al{sub}2O{sub}3/AlN composite powders[J].Journal of Materials Processing Technology,1999(0):392-398. |
| [3] | Sujanto Widjaja;Andi M. Limarga;Tick Hon Yip .Modeling of residual stresses in a plasma-sprayed zirconia/alumina functionally graded-thermal barrier coating[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):216-227. |
| [4] | Jingde ZHANG;Yansheng YIN;Jing LI;Hong Zhang .[J].Journal of Materials Processing Technology,2003,134(02):210. |
| [5] | M M Lima;C Godoy;P J Modenesi;J C Avelar-Batista,A Davison and A Matthews .[J].Surface and Coatings Technology,2004,177-178:489. |
| [6] | Lianmeng ZHANG.Material Science[M].北京:高等教育出版社,2005:123-134,153. |
| [7] | Shijun DENG .[J].Surface Engineering,2003,6(03):4. |
| [8] | Y R Liu;Traugott E Fischer;Andrew Dent .[J].Surface and Coatings Technology,2003,167:68. |
| [9] | S. Dallaire;D. Dube;M. Fiset .Laser melting of plasma-sprayed copper-ceramic coatings for improved erosion resistance[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(1):102-107. |
| [10] | Zeng LE.Modern Welding Technique Manual[M].上海:上海科学技术出版社,1993:867-869. |
| [11] | Zhuang MA;Guangshu LU;Fuchi WANG;Quansheng WANG.[J].Journal of Materials Engineering,2001(05):34. |
| [12] | Binshi XU;Shaohua ZHU;Shican LIU.Materials Surface Engineering[M].哈尔滨:哈尔滨工业大学出版社,2005:64-67. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%