以热电厂服役时间长达230000 h的主蒸汽管道X20马氏体耐热钢为研究对象,通过室温和服役高温的力学性能测试、组织以及亚结构和析出相的SEM、TEM观察、电解萃取相XRD物相分析等,研究了耐热钢长期服役的力学性能和显微结构变化.结果表明:服役钢除室温冲击性能下显著下降外,其他的力学性能退化并不显著.服役后材料的组织仍为典型的马氏体,但马氏体组织粗化明显,出现板条碎化,板条界移动,位错密度下降,碳化物粗化等现象.服役前后材料中碳化物形态和种类出现明显变化,耐热钢中主要碳化物M23C6长期服役后粗化显著,原始态中存在的亚稳态碳化物M2C及M6C和部分MX溶解,析出了Laves相和Z相.
参考文献
| [1] | HU Zheng-fei;YANG Zhen-guo;HE Guo-qiu et al.Damage and residual life assessment of bends for X20CrMoV12.1 main steam pipe after long term service[J].Journal of Failure Analysis and Prevention,2008,8(01):41-47. |
| [2] | Hu ZF;Yang ZG .An investigation of the embrittlement in X20CrMoV12.1 power plant steel after long-term service exposure at elevated temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(2):224-228. |
| [3] | A. Kostka;K.-G. Tak;R.J. Hellmig .On the contribution of carbides and micrograin boundaries to the creep strength of tempered martensite ferritic steels[J].Acta materialia,2007(26):539-550. |
| [4] | 赵彦芬,张路.高温管道用中Cr（F12类）钢的材质状态与热强性关系[J].中国电力,2008(10):57-61. |
| [5] | 胡正飞,杨振国,何国求,陈成澍.热电厂F12材质主蒸汽管道系统的寿命评价[J].同济大学学报(自然科学版),2008(01):86-91. |
| [6] | 胡正飞,吴细毛,张斌,陆传镇.长期服役的12%Cr马氏体耐热钢中的碳化物及其变化[J].动力工程学报,2010(04):269-274. |
| [7] | 陆传镇,胡正飞,赵俊韦,袁超.F12耐热钢服役过程中碳化物演变与蠕变空洞的形成[J].金属热处理,2011(03):41-45. |
| [8] | Leona Korcakova;John Hald;Marcel A.J. Somers .Quantification of Laves phase particle size in 9CrW steel[J].Materials Characterization,2001(2):111-117. |
| [9] | 张斌,胡正飞,王起江,陆传镇,王春亮,蒋凯雁.国产T91耐热钢650℃蠕变断裂微观机理[J].金属热处理,2010(09):41-46. |
| [10] | 张金旺;赵利平;王乐才 等.高温长期时效12%Cr钢中Cr23 C6变化规律研究[J].金属热处理学报,1996,17(01):16-20. |
| [11] | BAO Han-sheng,CHENG Shi-chang,LIU Zheng-dong,TAN Shu-ping.Aging Precipitates and Strengthening Mechanism of T122 Boiler Steel[J].钢铁研究学报（英文版）,2010(02):67-73. |
| [12] | 石如星,刘正东.P92钢中Laves相强化作用的研究[J].物理测试,2011(04):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%