采用圆柱试样在Gleeble-1500热模拟机上对喷射沉积7075Al/SiCp复合材料进行高温压缩变形实验,实验条件为:变形温度300～450℃,应变速率0.001～1s-1.结果表明:7075Al/SiCp复合材料的流变应力大小受到变形温度和应变速率的强烈影响,流变应力随应变的增加而逐渐增加,出现一峰值后逐渐下降;流变应力随变形温度的升高、应变速率的降低而降低.可用Zener-Hollomon参数的双曲正弦形式来描述7075Al/SiCp复合材料高温压缩变形流变应力.随着变形温度的升高和应变速率的降低,7075Al/SiCp复合材料热变形过程中SiCp的分布逐渐均匀化,有利其热加工性能的改善.
参考文献
| [1] | Liu Y B;Lim S C;Lu L .Recent development in the fabrication of metal matrix-particulate composites using powder metallurgy techniques[J].Journal of Materials Science,1994,29:1999. |
| [2] | Zhang D L;Brindley C;Cantor B .The microstructures of aluminum alloy metal-matrix composites manufactured by squeeze casting[J].Journal of Materials Science,1993,28:2267. |
| [3] | 陈振华,张豪,刘秋林,陈刚,孙章明,杨伏良.多层喷射共沉积法制备6066铝合金/SiC颗粒复合材料[J].中国有色金属学报,1996(04):83-86. |
| [4] | Franksu Y H;Chen Y C;Chi Y A et al.Workability of spray-formed 7075 Al alloy reinforced with SiCp at elevated temperatures[J].Materials Science and Engineering,2004,A364:296. |
| [5] | Goswami R K;Sikand R;Har A D et al.Extrution characteristics of aluminum alloy /SiCp metal matrix composites[J].Mater Techn,1999,15:443. |
| [6] | Zhao Mingjiu;Chen Liqing;Bi Jing .Effect of interlayer on the diffusion bonding of silicon carbon particulate reinforced 2024 aluminum composites[J].Journal of Materials Science and Letters,1999,18:2005. |
| [7] | Zhao Mingjiu;Chen Liqing;Bi Jing et al.Diffusion bonding of silicon carbon particulate reinforced 2024 aluminum composites[J].Journal of Materials Science and Technology,2000,16:471. |
| [8] | Yeh M S;Weng W P;Wang W S et al.Plastic flow behavior during the forging of a 6061-Al/10 Vol pct Al2O3 (p)composite[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31A:1310. |
| [9] | McQueen H J;Yue S;Ryan N D et al.Hot working characteristics of steels in austenitic state[J].Journal of Materials Processing Technology,1995,53:293. |
| [10] | 杨立斌,张辉,彭大暑,段炼.7075铝合金高温流变行为的研究[J].热加工工艺,2002(01):1-2,5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%