以玉米淀粉和马来酸酐(MAH)为原料,通过干法合成MAH酯化淀粉,通过熔融挤出法制备酯化淀粉/聚乳酸(PLA)复合材料.研究了MAH用量对复合材料结晶度和相容性的影响,同时考察了相容性和结晶度的变化对复合材料热性能、熔融流动性能、力学性能、耐水性能和流变性能的影响.FTIR结果证明通过干法成功合成了MAH酯化淀粉.酯化淀粉的取代度随MAH用量增多逐渐增大,反应效率高达90％.XRD和DSC结果表明:随着MAH用量增多,酯化淀粉/PLA复合材料的结晶度逐渐降低,淀粉和PLA的相容性逐渐提高.结晶度的降低和相容性的提高使复合材料的玻璃化转变温度逐渐降低,熔融流动性提高,耐水性提高.在力学性能和流变性能受相容性和结晶度的共同影响下,酯化淀粉中MAH用量从0增加到1.0wt％时,复合材料拉伸强度、弯曲强度、储能模量和复数黏度都逐渐增大,MAH用量超过1.0wt％后,性能逐渐降低.
参考文献
| [1] | 徐喻琼;瞿金平.可降解PLA/淀粉共混复合材料的研究进展[J].材料导报,200721(06):59-62. |
| [2] | Garlotta D.A literature review of poly (lactic acid)[J].Journal of Polymer and the Environment,20019(02):63-84. |
| [3] | Mehta R;Kumar V;Bhunia H.Synthesis of poly (lactic acid):a review[J].Journal of Macromolecular Science Part C:Polymer Reviews,200545(04):325-349. |
| [4] | Wang H;Sun X Z;Seib P.Strengthening blends of poly (lactic acid) and starch with methylenediphenyl diisocyanate[J].Journal of Applied Polymer Science,200182(07):1761-1767. |
| [5] | Zhang J F;Sun X Z.Mechanical properties of poly(lactie acid)/starch composites compatibilized by maleicanhydride[J].Biomacromolecules,20045(04):1446-1451. |
| [6] | Wang N;Yu J G;Ma X F.Preparation and characterization of thermoplastic starch/PLA blends by one-step reactive extrusion[J].Polymer International,200756(11):1440-1447. |
| [7] | 何东保;李青.直链淀粉和MAH酯的合成及性能研究[J].武汉大学学报(理学版),200349(02):193-196. |
| [8] | Huang L;Xiao C M;Chen B X.A novel starch-based adsorbent for removing toxic Hg(Ⅱ) and Pb(Ⅱ) ions from aqueous solution[J].Journal of Hazardous Materials,2011192(02):832-836. |
| [9] | 王金玲 .淀粉酯化及酯化淀粉/PCL共混物性能研究[D].武汉:华中农业大学,2006. |
| [10] | Xing G X;Zhang S F;Ju B Z.Microwave-assisted synthesis of starch maleate by dry method[J].Starch/Starke,200658(09):464-467. |
| [11] | Zuo Y F;Gu J Y;Yang L.Synthesis and characterization of maleic anhydride esterified cornstarch by the dry method[J].International Journal of Biological Macromolecules,201362:241-247. |
| [12] | GB/T 3682-2000.热塑性塑料熔体质量流动速率和熔体体积流动速率的测定[S].北京:中国标准出版社,2000. |
| [13] | ASTM D4440-08.Standard test method for plastics:dynamic mechanical properties melt rheology[S].New York:ASTM International,2008. |
| [14] | GB/T 1040-1992.塑料拉伸性能试验方法[S].北京:中国标准出版社,1992. |
| [15] | GB/T 9341-2008.塑料弯曲性能的测定[S].北京:中国标准出版社,2008. |
| [16] | GB/T 1034-2008.塑料吸水性的测定[S].北京:中国标准出版社,2008. |
| [17] | Dontulwar J R;Borikar D K;Gogte B B.An esteric polymer synthesis and its characterization using starch,glycerol and maleic anhydride as precursor[J].Carbohydrate Polymers,200665(02):207-210. |
| [18] | Ma X F;Chang P R;Yu J G.Preparation and properties of biodegradable poly (propylene carbonate)/thermoplastic dried starch composites[J].Carbohydrate Polymers,200871(02):229-234. |
| [19] | 樊国栋;陈春兰;刘香云.聚乙二醇改性PLA的合成与性能表征[J].功能材料,201041(02):238-240. |
| [20] | 由英才;朱常英;焦京亮.淀粉/DL-丙交酯接枝共聚物的合成和生物降解性能研究[J].高分子学报,200012(06):746-750. |
| [21] | Klug H P;Alezander L E.X-ray diffraction procedures for poly-crystalline and amorphous material[M].New York:Wily-Interscience,1974:74-89. |
| [22] | Sagar A D;Merril E W.Properties of fatty-acid esters of starch[J].Journal of Applied Polymer Science,199558(09):1647-1652. |
| [23] | 涂克华;王利群;王焱冰.淀粉接枝共聚物在淀粉/PLA共混体系中的作用[J].高分子材料科学与工程,200218(05):108-114. |
| [24] | Tsuji H;Ikada Y.Blends of crystalline and amorphous poly (lactide).Ⅲ.Hydrolysis of solution-cast blend films[J].Journal of Applied Polymer Science,199763(07):855-863. |
| [25] | Maiti S N;Hassan M R.Melt rheological properties of polypropylene-wood flour composites[J].Journal of Applied Polymer Science,198937(07):2019-2032. |
| [26] | 王全华;付中玉.熔融指数对聚丙烯熔体流动性及纤维强度的影响[J].北京服装学院学报,200424(04):27-31. |
| [27] | 费传军;赵谦;周昌玉.聚丙烯熔融指数对GMT力学性能的影响[J].玻璃纤维,2007(02):10-15. |
| [28] | 徐配弦.高聚物流变学及其应用[M].北京:化学工业出版社,2003:8-11. |
| [29] | Cassagnau P;Melis F.Non-linear viscoelastic behaviour and modulus recovery in silica filled polymers[J].POLYMER,200344(21):6607-6615. |
| [30] | 舒文艺;金日光.CPE对PVC/PP体系流变性能的影响[J].高分子材料科学与工程,19923(03):57-60. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%