采用自孕育法制备ZA96镁合金半固态组织,研究自孕育工艺参数对ZA96镁合金半固态组织的影响,并从温度场的角度分析工艺参数之间相互作用的本质.结果表明:采用自孕育法铸造,能够获得合格的半固态坯料和浆料.工艺参数对半固态坯料组织影响较大,但对从导流器出口处收集到的浆料在半固态区间进行保温后,发现自孕育剂加入量对组织影响不大,而导流器角度的影响较大.熔体过热度为80~95℃、自孕育剂加入量为5%、导流器角度为45°时,半固态坯料组织的晶粒平均尺寸较小,约为35.6μm;或经552℃、20 s保温后,其晶粒尺寸为45μm,圆整度为1.7.自孕育工艺参数交互作用的本质在于通过自孕育参数的调整从而达到控制其形核的目的.推导出了熔体在导流器出口处的温度与自孕育工艺参数之间的关系式.
@@@@Semi-solid microstructure of ZA96 magnesium alloy was prepared by self-inoculation method (SIM). The effects of self-inoculation technological parameters on the microstructure of semi-solid ZA96 magnesium alloy were investigated. And the nature of interactive effect between technological parameters was analyzed from the standpoint of temperature field. The results show that high-quality semi-solid billets and slurry can be obtained by SIM. The effects of self-inoculation technological parameters on the microstructure of semi-solid billets are bigger, but for the microstructure of semi-solid slurry which is collected from the exit of the fluid director and holding in semi-solid interval, the effect of self-inoculants is smaller, but that of the angle of fluid director is bigger. When the superheat of the melt is 80?95℃and the addition of self-inoculants is 5%and the angle of fluid director is 45°, the grain size of semi-solid billet is 35.6μm?or after holding 20 s at 552℃, the grain size of primary phase is 45μm and the roundness is 1.7. The interactive nature of self-inoculation technology parameters is to control nucleation by coordinating them. The formula between the temperature of melt in the exit of fluid director and self-inoculation technological parameters was derived.
参考文献
| [1] | LUO A A .Magnesium:current and potential automotive application[J].JOM,2002,54:42-48. |
| [2] | FLEMINGS M C .Behavior of metals and alloys in the semi-solid state[J].METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1991,22:957-981. |
| [3] | PAN Q Y;FINDON M;APELIAN D.The continuous rheoconversion process(CRP):A novel SSM approach[A].Limassol:North American Die Casting Association,2004 |
| [4] | YURKO J A;MARTINEZ R A;FLEMINGS M C.Development of semisolid rheocasting(SSR)[A].Tsukuba,Japan:National Institute of Advanced Industrial Science and Technology,2002:659-664. |
| [5] | Guo, HM;Yang, XJ .Efficient refinement of spherical grains by LSPSF rheocasting process[J].Materials Science and Technology,2008(1):55-63. |
| [6] | 路贵民,董杰,崔建忠,常守威.7075 Al合金液相线半连续铸造组织及形成机理[J].金属学报,2001(10):1045-1048. |
| [7] | H. Kaufmann;A. Mundl;R. Potzinger;P. J. Uggowitzer;N. Ishibashi .An update on the new rheocasting - development work for Al- and Mg-alloys[J].Die Casting Engineer,2002(4):16-19. |
| [8] | XING Bo,LI Yuan-dong,MA Ying,CHEN Ti-jun,HAO Yuan.Microstructure of partially remelted billet of AM60 alloy prepared with self-inoculation method[J].中国有色金属学报（英文版）,2010(09):1622-1629. |
| [9] | 曲俊峰,李元东,邢博,张鹏.自孕育法流变压铸AZ91D镁合金微观组织特征[J].铸造,2010(05):454-458. |
| [10] | 严楷,李元东,马颖,陈体军.熔体处理温度对自孕育法制备AZ61半固态浆料的影响[J].特种铸造及有色合金,2011(05):424-427. |
| [11] | 杨明波,PAN Fu-sheng,李忠盛,SHEN Jia.Zn与Al质量比对Mg-Zn-Al三元镁合金铸态组织和凝固行为的影响[J].中国有色金属学报,2008(07):1191-1198. |
| [12] | ZHANG Jing,LI Zhong-sheng,GUO Zheng-xiao,PAN Fu-sheng.Solidification microstructural constituent and its crystallographic morphology of permanent-mould-cast Mg-Zn-Al alloys[J].中国有色金属学会会刊（英文版）,2006(02):452-458. |
| [13] | XIAO Wen-long;SHEN Yu-sen;WANG Li-dong;WU Yao-ming CAO Zhan-yi JIA She-sheng WANG Li-min .The influences of rare earth content on the microstructure and mechanical properties of Mg-7Zn-5Al alloy[J].Materials and Design,2010,31:3542-3549. |
| [14] | 郭洪民 .半固态铝合金流变成形工艺与理论研究[D].南昌大学,2007. |
| [15] | 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000 |
| [16] | FLEMINGS M C;MARTINEZ R A .Principles of microstructure formation in semi-solid metal processing[J].Solid State Phenomena,2006,116/117(01):1-8. |
| [17] | 王建中 .电脉冲孕育处理技术与液态金属团簇结构假说的研究[D].北京:北京科技大学,1998. |
| [18] | 管仁国,康立文,尚剑洪,王超,温景林.倾斜式冷却剪切工艺条件对半固态合金组织的影响[J].特种铸造及有色合金,2005(10):600-603. |
| [19] | FLEMINGS M C .Behavior of metal alloys in the semi-solid state[J].Metallurgical Transactions B,1991,22(03):269-293. |
| [20] | 李庆春.铸件形成理论基础[M].北京:机械工业出版社,1982 |
| [21] | 董杰,路贵民,任栖锋,崔建忠.液相线铸造法非枝晶半固态组织形成机理探讨[J].金属学报,2002(02):203-207. |
| [22] | 李春,李元东,马颖,陈体军,武慧慧,李艳磊.熔体处理在制备Mg-9Zn-2Al镁合金半固态浆料中的作用[J].中国有色金属学报,2012(06):1536-1545. |
| [23] | 吴树森.材料加工冶金传输原理[M].北京:机械工业出版社,2001 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%