利用恒流充放电、交流阻抗和循环伏安法深入研究了电极片质量、粘结剂PTFE的含量、平压压力和电解液KOH浓度等超级电容器器件制作工艺对聚苯乙烯基层次孔炭材料的电化学性能的影响。结果表明这些器件制作工艺对层次孔炭材料的储电性能有非常大的影响。当电极片质量约为9mg,PTFE含量为8%,平压压力为4MPa,KOH浓度为4mol/L时,层次孔炭材料的储电容量最大,可达135F/g;而当器件制作工艺不佳时,其储电容量出现不同程度的下降,最差时仅为56F/g,为最优工艺的41%。
In this study,the relationship between supercapacitor preparation technique and electrochemical performance for polystyrene-based hierarchical porous carbon（HPC） had been studied in detail by means of constant charge/discharge measurements,impedance spectrum,cyclic voltammetric measurements,and so on.The techniques studied here include electrode preparation conditions like electrode weight,percentage of binder（PTFE） and pressing pressure,and concentration of electrolyte（KOH）.The experimental results showed that the techniques play an important role in the electrochemical properties of HPC.When the electrode weight,PTFE content,pressing pressure and KOH concentration were 9mg,8%,4MPa and 4mol/L,respectively,HPC exhibited the highest capacitance of 135F/g.However,when changing the techniques to the case of 9mg,8%,1MPa and 6mol/L,the specific mass capacitance was as low as 56F/g,only 41% of the above optimal value.
参考文献
| [1] | A. G. Pandolfe;A. F. Hollenkamp .Carbon properties and their role in supercapacitors[J].Journal of Power Sources,2006(1):11-27. |
| [2] | Largeot C;Portet C;Chmiola J;Taberna PL;Gogotsi Y;Simon P .Relation between the ion size and pore size for an electric double-layer capacitor[J].Journal of the American Chemical Society,2008(9):2730-2731. |
| [3] | Nam Dong Kim;Wooyoung Kim;Ji Bong Joo;Seogil Oh;Pil Kim;Younghun Kim;Jongheop Yi .Electrochemical capacitor performance of N-doped mesoporous carbons prepared by ammoxidation[J].Journal of Power Sources,2008(1):671-675. |
| [4] | Naoi K.;Suematsu S. .Electrochemistry of Poly(1,5-diaminoanthraquinone) and Its Application in Electrochemical Capacitor Materials[J].Journal of the Electrochemical Society,2000(2):420-426. |
| [5] | Da-Wei Wang;Feng Li;Min Liu .3D Aperiodic Hierarchical Porous Graphitic Carbon Material for High-Rate Electrochemical Capacitive Energy Storage[J].Angewandte Chemie,2008(2):373-376. |
| [6] | Cara M. Doherty;Rachel A. Caruso;Bernd M. Smarsly .Hierarchically Porous Monolithic LiFePO4/Carbon Composite Electrode Materials for High Power Lithium Ion Batteries[J].Chemistry of Materials: A Publication of the American Chemistry Society,2009(21):5300-5306. |
| [7] | Kaisheng Xia;Qiuming Gao;Jinhua Jiang .Hierarchical porous carbons with controlled micropores and mesopores for supercapacitor electrode materials[J].Carbon: An International Journal Sponsored by the American Carbon Society,2008(13):1718-1726. |
| [8] | Chong Zou;Dingcai Wu;Mingzhou Li .Template-free fabrication of hierarchical porous carbon by constructing carbonyl erosslinking bridges between polystyrene chains[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2010(4):731-735. |
| [9] | Liang, YR;Wu, DC;Fu, RW .Preparation and Electrochemical Performance of Novel Ordered Mesoporous Carbon with an Interconnected Channel Structure[J].Langmuir: The ACS Journal of Surfaces and Colloids,2009(14):7783-7785. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%