为改善 8YSZ 材料的力学性能,利用呈板片状结构的 LaMgAl11O19 来强韧化 8YSZ 陶瓷,在 1600 ℃下保温 3 h制备了LaMgAl11O19 -8YSZ 复相陶瓷,研究了 LaMgAl11O19 的添加量对 8YSZ 基复相陶瓷的致密度、显微形貌和力学性能的影响.结果表明,添加板片状 LaMgAl11O19可较明显地改善8YSZ陶瓷的力学性能.当 LaMgAl11O19 的添加量为 20 wt%时,8YSZ基复相陶瓷的抗弯强度和断裂韧性分别为297.4 MPa和4.0 MPa·m1/2.
参考文献
| [1] | Stambouli A B;Traversa E .Fuel Cells,an Alternative to standard Sources of Energy[J].Renewable & Sustainable Energy Reviews,2002,6(03):295-304. |
| [2] | C.K.Loong;M.Ozawa .The role of rare earth dopants in nanophase zirconia catalysts for automotive emission control[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(0):60-65. |
| [3] | Desouza S.;Dejonghe LC.;Visco SJ. .THIN-FILM SOLID OXIDE FUEL CELL WITH HIGH PERFORMANCE AT LOW-TEMPERATURE[J].Solid state ionics,1997(1/2):57-61. |
| [4] | Singhal SC. .Solid oxide fuel cells for stationary, mobile, and military applications[J].Solid state ionics,2002(Pt.A):405-410. |
| [5] | Kharton V V;Marques F M B;Atkinson A .Transport Properties of Solid Oxide Electrolyte Ceramics:a Brief Review[J].Solid-State Ionicis,2004,174:135-149. |
| [6] | Machida M;Eguchi K;Arai H .Analytical Electron Microscope Analysis of the Formation of BaO@6Al2O3[J].Journal of the American Ceramic Society,1988,71(12):1142-1147. |
| [7] | 尤洪鹏,吴雪艳,洪广言,卞锺洪,庾炳容.LaMgAl11O19∶R（R＝Tb,Mn）的真空紫外光谱特性[J].中国稀土学报,2002(06):572-574. |
| [8] | 王博宇,徐进章,陈昊,张志华.LaMgAl11O19：Mn2+和LaMgAl11O19：RE,Mn2+（RE=Eu2+,Gd3+）的发光特性[J].稀有金属材料与工程,2009(03):389-392. |
| [9] | 徐进章,张志华,王育华.LaMgAl11O19：Tb的助熔剂法制备及其发光特性[J].稀有金属材料与工程,2006(06):950-953. |
| [10] | A. Kulkarni;Z. Wang;T. Nakamura;S. Sampath;A. Goland;H. Herman;J. Allen;J. Ilavsky;G. Long;J. Frahm .Comprehensive microstructural characterization and predictive property modeling of plasma-sprayed zirconia coatings[J].Acta materialia,2003(9):2457-2475. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%