采用氨气鼓泡法制备TiO2/Mg(OH)2多功能复合材料,其中以钛酸正丁酯为前躯体,硝酸铵和九水硝酸铁为氮、铁掺杂源,利用水热法制备了氮、铁共掺杂TiO2粉体.通过XRD、FE-SEM、FT-IR、TG等手段对所制备样品进行了表征,结果表明:75℃条件下,通氨时间为1h,产品粒度分散均匀,二次粒径为0.69μm；产品形貌为六方片状；其(001)面与(101)面特征衍射峰的强度比值I001/I101为0.71；在322 ～ 396℃的分解失重为24.9％,最高吸热温度为376.2℃,技术指标符合氢氧化镁阻燃剂的使用要求；对罗丹明b溶液的光降解率为56.3％.
参考文献
| [1] | Michael R. Hoffmann;Scot T. Martin;Wonyong Choi;Detlef W. Bahnemann .Environmental Applications of Semiconductor Photocatalysis[J].Chemical Reviews,1995(1):69-96. |
| [2] | Kim J;Lee J;Choi W .Synergic effect of simultaneous fluorination and platinization of TiO2 surface on anoxic photocatalytic degradation of organic compounds[J].Chemical communications,2008(6):756-758. |
| [3] | Ohno, T;Tsubota, T;Toyofuku, M;Inaba, R .Photocatalytic activity of a TiO2 photocatalyst doped with C4+ and S4+ ions having a rutile phase under visible light[J].Catalysis Letters,2004(4):255-258. |
| [4] | T. Umebayashi;T. Yamaki;H. Itoh;K. Asai .Band gap narrowing of titanium dioxide by sulfur doping[J].Applied physics letters,2002(3):454-456. |
| [5] | 闫鹏飞,王建强,江欣,周德瑞,傅宏刚.掺铁TiO2纳米晶的制备及光催化性能研究[J].材料科学与工艺,2002(01):28-31. |
| [6] | 华南平,吴遵义,杜玉扣,邹志刚,杨平.Pt、N共掺杂TiO2在可见光下对三氯乙酸的催化降解作用[J].物理化学学报,2005(10):1081-1085. |
| [7] | 顾凌燕,王玉萍,彭盘英,王连军.S与金属共掺杂TiO2催化剂的制备及其光催化性能[J].中国有色金属学报,2009(05):910-918. |
| [8] | 陈建军,李俊华,柯锐,康守方,郝吉明.钒和钨负载量对V2O5-WO3/TiO2表面形态及催化性能的影响[J].环境科学,2007(09):1949-1953. |
| [9] | 郑振荣 .阻燃粘胶织物的组织结构及染整加工对其阻燃性能的影响研究[D].天津工业大学,2008. |
| [10] | 田从学,杨颖,蒲洪.工业钛液制备掺杂多孔二氧化钛及其光催化性能研究[J].钢铁钒钛,2011(03):1-6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%