本文采用HIP后处理技术,研究了不同温度下HIP后处理工艺对Al2O3陶瓷物理、机械性能及显微结构的影响.实验表明:Al2O3试样密度随HIP处理温度的升高而增加,1700℃时密度最高；试样的硬度经HIP处理后有提高,1500 ℃时硬度提高了8.62％;1500℃HIP处理后,抗弯强度达最大值,晶粒约2～8 μm,气孔变小变少；1800℃时,抗弯强度从HIP前的621MPa降低到349 MPa.根据上述研究结果,选择Al2O3人工髋关节作为应用对象,经HIP后处理,抗弯强度达到了636 MPa,密度达到了3.98 g/cm3.
参考文献
| [1] | Westerlund J .Four decades of HIP progress[J].Metal Powder Report,2000,2(55):15-21. |
| [2] | Westerlundet J .Hot isostatic pressing[J].International Journal of Powder Metallurgy,1999,3(25):267-270. |
| [3] | 谌启明,杨靖,单先裕,Jan Westerlund.热等静压技术的发展及应用[J].稀有金属与硬质合金,2003(02):33-38. |
| [4] | 佘继红;江东亮;郭景坤 .热等静压工艺在工程陶瓷中的应用与发展[J].无机材料学报,1999,11(03):396-406. |
| [5] | Hirano M.;Mizutani Y.;Nomura K.;Kawai M.;Nakamura Y.;Inagaki M. .Mechanical and electrical properties of Sc2O3-doped zirconia ceramics improved by postsintering with HIP[J].Solid state ionics,2000(1/2):1-9. |
| [6] | Dusan G;Jaroslav S .The influence of post-sintering HIP on the microstructure,hardness,and indentation fracture toughness of Al2O3-SiC nanocomposites[J].Journal of the European Ceramic Society,2007,27:1237-1245. |
| [7] | 王民权;王远忠.硅酸盐物理化学[M].北京:中国建筑工业出版社,1983:350-365. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%