以喷雾干燥-H2还原法制备的纳米级90W-7Ni-3Fe复合粉末为原料,采用模压成型并在800℃保温120min的条件下对试样进行预烧,研究了试样在不同烧结温度和不同烧结时间下的烧结特性,采用高倍SEM和光学金相分别对断口进行了形貌观察和钨晶粒测试;对烧结样的相对密度、抗拉强度、延伸率等性能进行了测定与分析.结果表明:保温时间为120 min时,随着烧结温度的提高,试样的性能有显著的变化,当烧结温度为1 390℃时,试样的抗拉强度和延伸率都达到一个极大值,分别为900 MPa和13%,此时试样的相对密度为99.0%;当烧结温度为1 390℃时,随着烧结时间的延长,试样的性能也有显著的变化,试样的抗拉强度、延伸率和相对密度都达到一个极大值;平均钨晶粒度为15～20 μm,钨晶粒呈球形或近球形;复合粉末烧结活性高,比传统烧结温度降低80～120℃;试样中出现了W30.73Ni40.21Fe29.06过渡相.
参考文献
| [1] | 黄继华;赖和怡;周国安 等.高比重钨合金的微观结构和性能的关系[J].粉末冶金技术,1992,10(01):63-68. |
| [2] | 马国刚.烧结时间对W-Ni-Fe重合金的组织结构及性能影响的研究[J].兵器材料科学与工程,2001(05):31-34. |
| [3] | Antonsson T;Ekbom L .Initial stage of liquid phase sintering: liquid reaction and particle growth in W-NiFe-(Co)[J].Powder Metallurgy,2001,44(03):325-331. |
| [4] | Liu Jian-xin;German R M .Microstructure effect on dihedral angle in liquid-phase sintering[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32:165-168. |
| [5] | Rabin B H;Bose A;German R M .Characteristics of liquid phase sintered tungsten heavy alloys[J].International Journal of Powder Metallurgy,1989,25(01):21-27. |
| [6] | H. FREDRIKSSON;A. ELIASSON;L. EKBOM .Penetration of Tungsten Grain Boundaries by a Liquid W-Ni-Fe Matrix[J].International Journal of Refractory Metals & Hard Materials,1995(4):173-179. |
| [7] | Cheynet M C .Strengthening of liquid phase sintered W-Ni-Fe base heavy alloys[J].International Journal of Refractory Metals and Hard Materials,1986,5(01):55-60. |
| [8] | 黄劲松,周继承,刘文胜,黄伯云.钨基重合金的烧结[J].粉末冶金工业,2003(01):26-29. |
| [9] | James R S;James A M .Tungsten Nickel Iron Alloys[P].US:5145512,1992. |
| [10] | Kim D K;Lee S H;Song H S .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1999,30(05):1261-1273. |
| [11] | Hogwood M C;Bentley A R.The development of high strength and toughness fibrous microstructure in tungsten-nickel-iron alloys for kinetic energy penetrator applications[A].Princeton:Metal Powder Industries Federation,1994:37-45. |
| [12] | 黄继华;周国安;赖和怡 等.近十年高比重钨合金强韧化研究动态[J].兵器材料科学与工程,1991,10:38-44. |
| [13] | Richard F C;韩凤麟.金属手册[M].北京:机械工业出版社,1994:532. |
| [14] | 张立德.纳米材料学[M].沈阳:辽宁科学技术出版社,1994:160. |
| [15] | 陈献峰,张晖,丁秉钧.纳米晶W粉的制备及烧结性能[J].稀有金属材料与工程,1998(05):294-297. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%