采用地衣酚（又称5-甲基间苯二酚,MR）——糠醛这一新的反应体系,用氢氧化钠作催化剂（C）,通过溶胶-凝胶工艺制备出了酚醛气凝胶.通过扫描电镜、比表面和孔径分析仪等仪器详细研究了工艺参数与气凝胶的骨架结构及孔结构的关系.结果表明：反应物质量含量对气凝胶骨架颗粒大小的影响较其他因素要大,而孔径分布则受反应物质量含量及酚与催化剂的摩尔比（MR/C）的影响较大.5-甲基间苯二酚——糠醛气凝胶平均孔径控制在5～20nm范围内,比表面积则在400～550g/m2范围内改变,较间苯二酚-糠醛气凝胶有较大提高.
Aerogels were prepared via sol-gel polymerization of a new reaction system（5-methylresorcinol-furfural） which was catalyzed by NaOH（C）.The relation of progress and aerogel structure was investigated by SEM and Surface Area and Pore Size Analyzer.The results show that mass content of reactants influences the particle siza more greatly.Pore size distribution changes greatly with mass content of reactants and MR/C（molar ratio）.The average pore diameter is about 5~20nm,and the surface aera is about 400~550g/m2,which is more larger than that of resorcinol-furfural aerogel.
参考文献
| [1] | 计亚军,何建平,周建华,党王娟,刘晓磊,张传香,赵桂网.添加过渡金属元素碳气凝胶的制备及性能[J].材料科学与工艺,2009(04):556-560. |
| [2] | 巢亚军,原鲜霞,杜娟,邓晓燕,马紫峰.炭气凝胶在电化学能源材料中的应用研究进展[J].材料科学与工艺,2009(04):492-495. |
| [3] | Jirglova, H;Perez-Cadenas, AF;Maldonado-Hodar, FJ .Synthesis and Properties of Phloroglucinol-Phenol-Formaldehyde Carbon Aerogels and Xerogels[J].Langmuir,2009(4):2461-2466. |
| [4] | 龙东辉,张洁,杨俊和,胡子君,李同起,成果,张睿,凌立成.苯酚-间甲酚-糠醛基炭气凝胶的制备及微结构控制[J].新型炭材料,2008(02):165-170. |
| [5] | 欧阳玲,沈军,周斌,侯今强,宓轶捷,张志华,吴广明.用于储氢材料的碳/掺杂碳气凝胶研究[J].原子能科学技术,2008(05):423-427. |
| [6] | 徐翔,周斌,杜艾,刘春泽,沈军,吴广明,倪星元,张志华.微尺寸碳气凝胶的制备及其机械性能研究[J].原子能科学技术,2008(z1):26-30. |
| [7] | Mirzaeian, M;Hall, PJ .The control of porosity at nano scale in resorcinol formaldehyde carbon aerogels[J].Journal of Materials Science,2009(10):2705-2713. |
| [8] | 秦仁喜,沈军,吴广明,周斌,王琴,倪星元,郭艳芝.碳气凝胶的常压干燥制备及结构控制[J].过程工程学报,2004(05):429-433. |
| [9] | Dingcai Wu;Ruowen Fu;Mildred S.Dresselhaus .Fabrication and nano-structure control of carbon aerogels via a microemulsion-templated sol-gel polymerization method[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(4):675-681. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%