采用纳米ZnO(nano-ZnO)对不饱和聚酯树脂(UPR)进行改性,研究nano-ZnO添加量对nano-ZnO/UPR复合体系综合性能的影响。结果表明:nano-ZnO对UPR具有明显的增强增韧作用,随着nano-ZnO添加量的增加,nano-ZnO/UPR复合体系的黏度和凝胶时间随之增大,拉伸强度、弯曲强度和冲击强度均呈先增大后减小的趋势,吸水率呈先减小后增大趋势,当添加量为5%时,nano-ZnO/UPR复合体系的综合性能最好,固化反应的表观活化能(E)为51.6 kJ/mol,反应级数(n)为0.892。

Unsaturated polyester resin (UPR) was modified by nano-ZnO, and the effect of nano-ZnO addi-tion on the comprehensive properties of the nano-ZnO/UPR composite system was studied. The results show that the nano-ZnO has an obvious reinforcing and toughening effect on the UPR. With the increase of the nano-ZnO additive amount, the viscosity and gel time of the nano-ZnO/UPR composite system in-crease, the tensile strength, flexural strength, and impact strength increase at first and then decrease, and the water absorption decreases first and then increases. When the additive amount of nano-ZnO is 5%, the comprehensive properties of the nano-ZnO/UPR composite system are the best, the apparent activation energy(E) of curing reaction is 51.55 kJ/mol, and the reaction order(n) is 0.892.

参考文献

[1] 魏珂瑶,周莉,张建中,张林.无机纳米粒子-不饱和聚酯树脂复合材料的研究进展[J].化学与黏合,2012(06):58-60.
[2] 李毅,唐安斌,黄杰,马寒冰.磷腈改性不饱和聚酯树脂的阻燃及耐热性能研究[J].绝缘材料,2014(4):33-36.
[3] 卢凤英,吕建,胡舒龙,章震,刘华山,曾德明.SBA-15/不饱和聚酯树脂的制备及其性能研究[J].绝缘材料,2014(02):41-44.
[4] Chirayil C J;Mathew L;Hassan P A et al.Rheological Be-haviour of Nanocellulose Reinforced Unsaturated Polyester Nanocomposites[J].International Journal of Biological Macro-molecules,2014,69:274-281.
[5] Chirayil, C. J.;Joy, J.;Mathew, L.;Koetz, J.;Thomas, S..Nanofibril reinforced unsaturated polyester nanocomposites: morphology, mechanical and barrier properties, viscoelastic behavior and polymer chain confinement.[J].Industrial Crops and Products,2014:246-254.
[6] Kayatin, MJ;Davis, VA .Viscoelasticity and Shear Stability of Single-Walled Carbon Nanotube/Unsaturated Polyester Resin Dispersions[J].Macromolecules,2009(17):6624-6632.
[7] M.T. Albdiry;H. Ku;B.F. Yousif.Impact fracture behaviour of silane-treated halloysite nanotubes-reinforced unsaturated polyester[J].Engineering failure analysis,2013:718-725.
[8] M.T. Albdiry;B.F. Yousif .Morphological structures and tribological performance of unsaturated polyester based untreated/silane-treated halloysite nanotubes[J].Materials & design,2013(Jun.):68-76.
[9] Javad Moftakharian Esfahani;Ali Reza Sabet;Masoud Esfandeh .Assessment of nanocomposites based on unsaturated polyester resin/nanoclay under impact loading[J].Polymers for advanced technologies,2012(4):817-824.
[10] Kaffashi, B.;Honarvar, F.M. .The effect of nanoclay and MWNT on fire-retardency and mechanical properties of unsaturated polyester resins[J].Journal of Applied Polymer Science,2012(2):1154-1159.
[11] Manila Chieruzzi;Adio Miliozzi;Jose M. Kenny .Effects of the nanoparticles on the thermal expansion and mechanical properties of unsaturated polyester/clay nanocomposites[J].Composites, Part A. Applied science and manufacturing,2013(2):44-48.
[12] Zhang M;Singh R P .Mechanical Reinforcement of Unsatu-rated Polyester by Al2O3 Nanoparticles[J].Materials Letters,2004,58(3):408-412.
[13] 周莉,张建中,吴海艳.不饱和聚酯树脂/纳米ZnO挡风抑尘板的制备[J].合成树脂及塑料,2013(03):61-65.
[14] Marco Monti;Debora Puglia;Maurizio Natali;Luigi Torre;Jose M. Kenny .Effect of carbon nanofibers on the cure kinetics of unsaturated polyester resin: Thermal and chemorheological modelling[J].Composites science and technology,2011(12):1507-1516.
[15] 王庆,王庭慰,魏无际.不饱和聚酯树脂固化特性的研究[J].化学反应工程与工艺,2005(06):492-496.
[16] Gao Y J;Li Y Z .Curing Behavior and Kinetic Analysis of Large Resin Content Resol[J].Polymer Letter Edition,1973,11(8):533-540.
[17] 张衍,刘育建,王井岗,韩哲文.DSC对苯基苯酚改性酚醛树脂固化机理研究[J].固体火箭技术,2007(02):142-145.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%