依据NACE标准研究了X80级管线钢的抗硫化物应力腐蚀开裂(SSCC)和氢致开裂(HIC)行为.研究表明该X80级管线钢具有较好的抗SSCC和HIC性能,其中临界名义应力S.达到:1 265 MPa;裂纹敏感率、裂纹长度率和裂纹厚度率均为0;酸性环境下氢的扩散以及应力集中的交互作用导致材料的韧性损失,从而促使裂纹的形成和扩展,最终导致材料断裂.以均匀细小的针状铁素体为主的显微组织具有优良的抗SSCC&HIC性能.
参考文献
| [1] | Chu W Y;Qiao L J;Chen Q Z.Fracture and Environmental Fractu re[M].北京:科学出版社,2000 |
| [2] | NACE Standard TM 0177-2005,Laboratory Testing of Metals for Resistance to Specific Forms of Environmental Cracking in H2S Environment[S].,2005. |
| [3] | NACE Standard TM 0284-2003,Evaluation of Pipeline and pressure Vessel Steels for Resistance to Hydrogen-Induced Cracking[S].,2003. |
| [4] | 殷光虹,施青,孙元宁.管线用钢氢致裂纹（HIC）影响因素分析[J].钢管,2004(06):20-26. |
| [5] | 李云涛,杜则裕,陶勇寅,熊林玉.X70管线钢硫化氢应力腐蚀[J].焊接学报,2003(03):76-78,86. |
| [6] | Perez T E;Quintanilla H;Rey E.Effect of Ca/s Ratio HIC Resistance of Seamless Line[J].Corrosion,1998(121):185. |
| [7] | Osella A;Favetto A;Lopez E .Corrosion Rates of Buried Pipelines due to Geomagnetic Storms[J].Corrosion,1999,55(07):699. |
| [8] | 李鹤林;郭生武;冯耀荣.高强度微合金管线钢显微组织分析与鉴别图谱[M].北京:石油工业出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%