Room temperature tensile tests of Fe-Mn-Al-C low density steels with four different chemical compositions were conducted to clarify the dominant deformation mechanisms.Parameters like product of strength and elongation, as well as specific strength and curves of stress-strain relations were calculated.The microstructures and tensile frac-ture morphologies were observed by optical microscope,scanning electron microscope and transmission electron mi-croscope.The tensile behavior of low density steel was correlated to the microstructural evolution during plastic de-formation,and the effects of elements,cooling process and heat treatment temperature on the mechanical properties of the steels were analyzed.The results show that the tensile strength of steels with different cooling modes is more than 1 000 MPa.The highest tensile strength of 28Mn-12Al alloy reached 1 230 MPa,with corresponding specific strength of 189.16 MPa.cm3 .g-1 ,while the specific strength of 28Mn-10Al alloy was 178.98 MPa.cm3 .g-1 , and the excellent product of strength and elongation of 28Mn-8Al alloy was over 69.2 GPa.%.A large number of ferrite reduced the ductility and strain hardening rate of the alloy,while the existence ofκcarbides may improve the strength but weaken the plasticity.Some fineκcarbides appeared in the water-quenched specimen,while coarseκcarbides were observed in the air-cooled specimen.High temperature heat treatment improved the decomposition ki-netics ofγphase and the diffusion rate of carbon,thus speeded up the precipitation of fineκcarbides.The dominant deformation mechanism of low density steel was planar glide,including shear-band-induced plasticity and microband-induced plasticity.