采用熔融共混法制备了聚丙烯(PP)/磷酸锆(OZrP)膨胀型阻燃材料,热重分析表明添加OZrP的阻燃体系成炭量有所增加.当PP基体中含有25%膨胀型阻燃剂(IFR)时,复合材料的氧指数为33,垂直燃烧测试为UL-94 V-1级别,当保持添加剂总量不变时,添加3%OZrP到PP/IFR体系中,氧指数增加到37,垂直燃烧达到V-0级别.IFR与OZrP间存在协效作用,合适的添加比例有利于提高复合材料的阻燃性能.
参考文献
| [1] | 谢飞,赵娇,杨冰,王玉忠.金属络合物用于聚乙烯催化阻燃研究[C].2005全国阻燃学术年会论文汇编,2005:99-102. |
| [2] | 彭治汉.材料阻燃新技术新品种[M].北京:化学工业出版社,2004:3. |
| [3] | Ye, L;Wu, QH;Qu, BJ .Synergistic Effects of Fumed Silica on Intumescent Flame-Retardant Polypropylene[J].Journal of Applied Polymer Science,2010(6):3508-3515. |
| [4] | 李俊;万军喜;唐国翌 .氢氧化镁阻燃聚丙烯体系的性能研究[J].材料导报:研究篇,2009,23(06):11. |
| [5] | Yuan Liu;Zhiqiang Feng;Qi Wang .The Investigation of Intumescent Flame-Retardant Polypropylene Using a New Macromolecular Charring Agent Polyamide 11[J].Polymer Composites,2009(2):221-225. |
| [6] | Peng Huaqiao;Zhou Qian;Wang Yuzhong .A novel charring agent containing caged bicyclic phosphate and its application in intumescent flame retardant polypropylene systems[J].Journal of Industrial and Engineering Chemistry,2008,14(05):589. |
| [7] | Zhang Feng;Zhang Jun;Jiao Chuanmei .Study on char str-ucture of intumescent flame-retardant polypropylene[J].Polym-Plastics Techn Eng,2008,47(11):1179. |
| [8] | 吴娜,杨荣杰,郝建薇,刘国胜.金属氧化物对聚丙烯膨胀阻燃体系阻燃性能的影响[J].高分子学报,2009(12):1205-1210. |
| [9] | Menachem Lewin;Makoto Endo .Catalysis of intumescent flame retardancy of polypropylene by metallic compounds[J].Polymers For Advanced Technologies,2003,14(01):3. |
| [10] | 孔庆红 .聚合物/铁蒙脱土纳米复合材料的制备及阻燃机理研究[D].中国科学技术大学,2006. |
| [11] | 张蕤,胡源,汪世龙.层状化合物α-磷酸锆的有机化处理[J].稀有金属材料与工程,2006(z2):100-103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%