通过采用扫描电镜、透射电镜及电子能谱等分析测试技术,研究了高铌管线钢的显微组织特征和析出相种类、大小及形态.结果表明,采用控轧控冷工艺(TMCP)生产的高铌管线钢具有细化的显微组织和多种类型的析出相,显微组织主要为高位错密度的针状铁素体、少量多边形铁素体和MA岛；第二相粒子主要包括板坯再加热过程中未溶解的TiN、以TiN为核心的高温析出NbC、形变诱导析出的NbC和低温弥散析出的细小NbC.细化的有效晶粒尺寸,以及高密度位错与弥散析出相间的交互作用,确保了高铌管线钢获得高的强度和韧性.
参考文献
| [1] | Douglas,Stalheim G.The Use of High Temperature Processing(HTP) Steel for High Strength Oil and Gas Transmission Pipeline Applications[A].中国,2005:703. |
| [2] | 郑磊,高珊,章传国,张备,李延丰.西气东输二线用高Nb X80级管线钢宽厚板的开发[J].焊管,2009(04):25-29,34. |
| [3] | Zhao M C;Yang K;Xiao F R;Shan Y Y .Continuous Cooling Transformation of Undeformed and Deformed Low Carbon Pipeline Steels[J].Materials Science and Engineering,2003,A355:126. |
| [4] | Norberg H;Aronsson B.Solubility of Niobium Carbide in Austenite[M].JISI,1968:1263. |
| [5] | Cuddy L J.Thermomechanical Processing of Microalloyed Austenite[M].TMS,Warrendale (PA),1982:129. |
| [6] | Speer J G;Hansen S S .Austenite Recrystallization and Carbonitride Precipitation in Niobium Microalloyed Steels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1989,20(01):25. |
| [7] | DeArDo A J.Accelerated Cooling:A Physical Metallurgy Perspective[A].Winnipeg,Canada,1987:1. |
| [8] | ZHENG Lei;GAO Shan .Production and Application of High Strength and High Toughness Pipeline Steel with Acicular Ferrite[J].Iron & Steel Supplement,2005,40(11):688. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%