以对水和空气稳定的离子液体1-乙基-3-甲基咪唑三氟甲磺酸盐([emim]OTf)为电解质,在不锈钢双极板表面电沉积铌,并在模拟质子交换膜燃料电池(PEMFC)环境中研究了镀铌改性的双极板的电化学行为.结果表明,铌镀层以孤岛的形式均匀分布在不锈钢表面,其高度在100 nm以内.XPS、XRD测试结果表明,镀铌不锈钢表面生成化学惰性良好的NbO、Nb2O5.在模拟阳极环境中,镀铌不锈钢的腐蚀电位比不锈钢的腐蚀电位提高530 mV;恒电位-0.1 V时电流密度从4.5315μA.cm-2降低到2.7554 μA·cm-2;在模拟阴极环境中,镀铌不锈钢的腐蚀电位比不锈钢提高430 mV,恒定电位0.6 V时电流密度从4.4008 μA.cm-2降低到0.0028 μA.cm-2.电化学测试结果表明,镀铌不锈钢的电化学极化性能得到改善,反应电阻增大,提高了耐蚀性能.
参考文献
| [1] | Wind J et al.[J].Journal of Power Sources,2002,105(02):256. |
| [2] | Zhang J et al.[P].US Patent,0033408-A 1,2004. |
| [3] | Masahiro Seo et al.[J].Corrosion Science,1986,26(11):949. |
| [4] | Neusa Alonso-Falleiros;Stephan Wolynec .[J].Materials Research,1998,1(01):39. |
| [5] | Weil K S et al.[J].International Journal of Hydrogen Energy,2007,32(16):3724. |
| [6] | Sung-Tae Hong K;Scott Weil .[J].Journal of Power Sources,2007,168(05):408. |
| [7] | Annealing induced interfacial layers in niobium-clad stainless steel developed as a bipolar plate material for polymer electrolyte membrane fuel cell stacks[J].Journal of Power Sources,2010(9):2592. |
| [8] | Koura N et al.[J].J Surf Finish Soc Jpn,1994,45(04):805. |
| [9] | Stafford G.Electrochemical Science and Engineering[M].Weinheim:Wiley-VCH,2002:291. |
| [10] | Stafford G R;Haarberg G M.[J].Plasmas & Ions,1999(01):35. |
| [11] | Liu H T;Xia X .[J].Acta Chimica Sinica,2000,58(08):992. |
| [12] | Ren Y J;Chen J et al.[J].Journal of Power Sources,2010,195:1914. |
| [13] | 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:北京科学技术出版社,2002:26. |
| [14] | Wind J et al.[J].Journal of Power Sources,2002,105(03):256. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%