研究了过共晶Al-17Si-xLa合金在室温下不同频率的阻尼-应变振幅行为.Al-17Si-xLa合金通过常规的铸造和喷射成形工艺制备,并采用动态热机械分析仪(DMTA)对其阻尼行为进行研究.结果表明大多数铸态以及喷射成形态Al-17Si-xLa合金显示了类似的室温应变振幅-阻尼行为:即随振幅的增加,阻尼先不增大,然后明显升高出现阻尼峰,最后回落,可以用G-L位错阻尼理论加以解释;铸态下添加La对Al-17Si合金的阻尼行为影响不大,过量La(6%(质量分数))添加明显降低阻尼性能.La的添加明显提高喷射成形态Al-Si合金阻尼性能.喷射成形态Al-Si合金的阻尼明显比相应铸态Al-Si合金的阻尼高.
参考文献
| [1] | Zhou J;Duszczyk J;Korevaar B M .[J].Journal of Materials Science,1991,26:3041-3050. |
| [2] | Sano H .[J].Metal Powder Report,1994(49):26-31. |
| [3] | Ye B J;Loper C R Jr;Lu D Y .[J].AFS Transactions,1985,30:533-544. |
| [4] | Yamauchi I;Ohnaka I;Kawamoto S et al.[J].Transactions of the Japan Institute of Metals,1986,27:195-203. |
| [5] | Zhang J;Eerez R J;Wong C R et al.[J].Materials Science and Engineering,1994,R13:325-390. |
| [6] | Batist R De.Internal Friction of Structural Defects in Crystalline Solids[M].Amsterdam: North-Holland,1972 |
| [7] | Zhang J;Gungor M N;LAVERNIA E J .[J].Journal of Materials Science,1991,28:1515-1524. |
| [8] | Lavernia E J;Zhang J;Perez R J.[J].Key Engineering Materials,1995:691-728. |
| [9] | Dutta I;Bourell D L .[J].Materials Science and Engineering,1989,112A:67-77. |
| [10] | Weiss J C;Loper C R Jr .[J].AFS Transactions,1987,32:51-62. |
| [11] | Chang JY.;Choi CS.;Moon IG. .Refinement of cast microstructure of hypereutectic Al-Si alloys through the addition of rare earth metals[J].Journal of Materials Science,1998(20):5015-5023. |
| [12] | Chang J Y;Kim G H;Moon I G et al.[J].Scripta Materialia,1998,39:307-314. |
| [13] | 孙伟成;张淑荣;侯爱芹.稀土在铝合金中的行为[M].北京:兵器工业出版社,1992 |
| [14] | Zhang M G;Chang Z L;Yan J M et al.[J].Journal of Materials Processing Technology,2001,115:294-297. |
| [15] | Kê T S;Cui P;Su C M .[J].Physica Status Solidi A,1984,84(01):157-164. |
| [16] | Cai W D;Smugeresky J;LAVERNIA E J .[J].Materials Science and Engineering,1998,A241:60-71. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%