采用两种不同素坯成型工艺制备层状C/ZrB2-SiC复合材料,并对其微观结构和力学性能进行研究.结果表明:高温下预压成型制备的层状ZrB2-SiC复合材料层厚均匀,界面平直,弯曲强度和断裂韧性较高,分别达到427MPa和11.3 MPa·m1/2.而室温下预压成型各层厚度不均,界面弯曲,出现界面交叉现象,弯曲强度和断裂韧性较低,分别为277 MPa和9.4 MPa·m1/2.采用素坯高温预压成型制备的层状C/ZrB2-SiC复合材料力学性能较高,主要归因于界面平直,裂纹交替通过基体层和界面层,裂纹的扩展路径变长,断裂功增加.
参考文献
| [1] | Wei-Ming Guo;Guo-Jun Zhang .Oxidation resistance and strength retention of ZrB_2- SiC ceramics[J].Journal of the European Ceramic Society,2010(11):2387-2395. |
| [2] | Haitang Wu;Weigang Zhang .Fabrication and properties of ZrB2-SiC-BN machinable ceramics[J].Journal of the European Ceramic Society,2010(4):1035-1042. |
| [3] | 吴世平,杨飞宇,张幸红,杜善义.碳短纤维对ZrB2-SiC基超高温陶瓷力学性能的影响[J].材料工程,2007(05):15-18. |
| [4] | Qilong Guo;Junguo Li;Qiang Shen .Preparation, microstructure, and mechanical properties of ZrB_2-based ceramics with layered Zr_2Al_4C_5 inclusions[J].CERAMICS INTERNATIONAL,2013(3):2215-2222. |
| [5] | 李冬云,乔冠军,金志浩.SiC/C层状陶瓷的断裂行为研究[J].稀有金属材料与工程,2003(08):635-638. |
| [6] | Xu Yongdong;Cheng Laifei;Zhang Litong .Carbon /silicon carbide composites prepared by chemical vapor infiltration combined with silicon melt infiltration[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(8):1179-1187. |
| [7] | G. de Portu;L. Micele;G. Pezzotti .Laminated ceramic structures from oxide systems[J].Composites, Part B. Engineering,2006(6):556-567. |
| [8] | Xiao-Jun Zhou;Guo-Jun Zhang;Yao-Gang Li .Hot pressed ZrB_2-SiC-C ultra high temperature ceramics with polycarbosilane as a precursor[J].Materials Letters,2007(4/5):960-963. |
| [9] | Rezaie A;Fahrenholtz WG;Hilmas GE .Effect of hot pressing time and temperature on the microstructure and mechanical properties of ZrB2-SiC[J].Journal of Materials Science,2007(8):2735-2744. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%