Ball Milling Synthesis and Property of Nd0.7Sr0.3MnO3 Manganites

材料科学技术（英文）, 2010, 26(8): 721-724.

^1, , ^2, , ^3, , ^4,

1.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

2.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

3.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

4.Department of Physics,Nanjing University,Nanjing 210093,China

基金项目: the joint Chinese-Russian Project for their financial supports the National Natural Science Foundation of China(10774040)

Ball Milling Synthesis and Property of Nd0.7Sr0.3MnO3 Manganites

Shunsheng Chen ^1, , Changping Yang ^2, , Lingfang Xu ^3, , Shaolong Tang ^4,

1.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

2.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

3.The Provincial Key Laboratory of Piezoelectric Ceramics Materials and Apparatus,Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062,China

4.Department of Physics,Nanjing University,Nanjing 210093,China

Keywords： High-energy ball milling

Strontium doped perovskite-type Nd0.7Sr0.3MnO3 ceramics were synthesized completely by high-energy ball milling raw oxides of Nd2O3,SrCO3 and MnO2. The optimal ball milling time and mass ratio of milling balls to raw materials are 4 h and 10:1,respectively. The grain size of as-milled Ndo.TSr0.3MnO3 ceramics ranges from 51 to 93 nm,and the fine particles contain two phases of crystalline phase and amorphous phase. For the Nd0.7Sr0.3MnO3 synthesized by ball milling and sequent heat treatment,a remarkable colossal electroresistance (CER) effect is observed and the CER ratio reaches 900% at Curie temperature Tc when the load voltage increases from 0.1 to 0.8 V.

参考文献

[1]	R. Gross;L. Alff;B. Buechner .Physics of grain boundaries in the colossal magnetoresistance manganites[J].Journal of Magnetism and Magnetic Materials,2000(1/3):150-159.
[2]	X.L. Zhang;Y.G. Zhao;Y.H. Sun .Thickness dependence of electroresistance in La_(0.67)Ca_(0.33)MnO_3 epitaxial films[J].Journal of Magnetism and Magnetic Materials,2006(1):55-59.
[3]	Y.Q. Ma;Z.Q. Sun;M.Z. Wu .Significant electroresistance effect tuned by oxygen stoichiometry in La_(0.5)Ca_(0.5)MnO_z[J].Solid State Communications,2007(4/5):245-249.
[4]	Y.Q. Ma;Z.Q. Sun;M.Z. Wu .Significant electroresistance effect tuned by oxygen stoichiometry in La_(0.5)Ca_(0.5)MnO_z[J].Solid State Communications,2007(4/5):245-249.
[5]	M. Muroi;R. Street;P. G. McCormick .Enhancement of critical temperature in fine La_(0.7)Ca_(0.3)MnO_(3) particles prepared by mechanochemical processing[J].Journal of Applied Physics,2000(7):3424-3431.
[6]	S.S. Chen;C.P. Yang;Z.H. Zhou .Synthesis of Nd_(0.7)Sr_(0.3)MnO_3 ceramics by high-energy ball milling[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2008(1/2):271-274.

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%