在工业试验的基础上,对高碳钢大方坯实施轻压下后铸坯中心区域产生严重的负偏析与微弱的正偏析的形成机制进行了探讨与分析,研究发现:铸坯实施轻压下后,优先生长的上下两层的树枝晶会在外力的作用下发生碰撞、折断破碎,折断破碎的细小晶粒在钢液的强迫流动作用下随机漂流到铸坯中心区域成为新的晶核,从而使其周围钢液先凝固,形成负偏析;此后富集元素钢液凝固形成微弱的正偏析.
参考文献
| [1] | Bridge M R;Rogers G D .Structural Effects and Band Segregation Formation During Electromagnetic Stirring[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1984,15B(09):581. |
| [2] | Kor G J W .Influence of Circumferential Electromagnetic Stirring on Macro Segregation in Steel[J].Ironmaking and Steelmaking,1982,9(06):244. |
| [3] | 轴承钢连铸坯碳偏析的形成机理及影响因素[J].北京科技大学学报,1999(02):131. |
| [4] | Reynolds T;Harvey A.Innovation in Slab Casting[A].Nashville:ISS-AIME,2002:41. |
| [5] | Oh K S;Park J K;Change S H.Development of Soft Reduction Technology for the Bloom Caster at Pohang Works of POSCO[A].Nashville:ISS-AIME,1995:301. |
| [6] | 陈永.重轨钢连铸的质量控制[J].钢铁,2004(03):23-26. |
| [7] | 蔡开科.连续铸钢[M].北京:科学出版社,1990 |
| [8] | 邢书明;陈维视;孙士宝.挤压铸造高锰钢的宏观质量及性能[J].铸造,1998(06):10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%