Local chemistry plays an important role in determining the cohesive strength of grain boundaries in Ni3Al. Doping with B increases the room temperature ductility and changes the fracture mode from intergranular to transgranular, while doping with Zr increases the ductility but leaves the fracture mode predominantly intergranular.Electron Energy Loss Spectroscopy (EELS) and Energy Dispersive X-ray Spectroscopy (EDS) were used to probe the changes in local bonding (and hence the cohesive strength) produced by changes in local chemistry at large angle boundaries in Ni3Al.In addition , small angle tilt boundaries were studied to correlate structure with Nienrichment at the interface. B segregation to Ni-rich grain boundaries was shown to make the bonding similar to that of the bulk, thereby increasing their fracture resistance. Ni-enrichment does not occur in the presence of Zr segregation to grain boundaries. Ni-enrichment to antiphase boundaries (APB) in small angle tilt boundaries lowers the APB energy by reducing the number of high energy Al-Al interactions across the interface. Ni-enrichment to large angle boundaries is expected to produce a similar effect on energy.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] | |
| [15] | |
| [16] | |
| [17] | |
| [18] | |
| [19] | |
| [20] | |
| [21] | |
| [22] | |
| [23] | |
| [24] | |
| [25] | |
| [26] | |
| [27] | |
| [28] | |
| [29] | |
| [30] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%