M40 carbon fibre reinforced rare earth magnesium alloy ZM6 composites with fibre volume fraction about 60%were fabricated by pressure infiltration method.The microstructure, interfacial morphology, and precipitation were studied by scanning electron microscopy, transmission electron microscopy, and energy dispersive Xray spectrometer.It was shown that the interfaces between Mg alloy and fibres were well bonded and free from cracks.The Mg12Nd phase was preferentially precipitated at the fibre/matrix interfaces, leading to the segregation of Nd at the interfaces and the dramatic decrease of Mg12Nd precipitation in the matrix far from interfaces.Crystal defects such as high-density dislocations and twins were observed in the matrix near the fibre/matrix interface.A high bending strength (1393 MPa) and elastic modulus (190 GPa) were achieved in M40/ZM6 composite.
参考文献
| [1] | S.Y. Chang,Y.L.Kim.Effect of Aging Treatment on Microstructural and Mechanical Characteristics of PEO Coatings on Mg-Al Alloy[J].材料科学技术学报（英文版）,2008(01):37-40. |
| [2] | C K(o)rner;W Sch(a)ff .[J].Advances in Engineering Materials,2000,6:327. |
| [3] | A Feldhoff;E Pippel .[J].Advances in Engineering Materials,2002,8:471. |
| [4] | S Ochiai;H Okuda .[J].Journal of Materials Science,2003,38:1737. |
| [5] | W. Hufenbach;M. Andrich;A. Langkamp .Fabrication technology and material characterization of carbon fibre reinforced magnesium[J].Journal of Materials Processing Technology,2006(1/3):218-224. |
| [6] | M Russell-Stevens;R Todd .[J].Surface and Interface Analysis,2005,27:336. |
| [7] | M Russell-Stevens;R Todd .[J].Materials Science and Engineering,2005,397:249. |
| [8] | M Russell-Stevens;R Todd .[J].Journal of Materials Science,2006,41:6228. |
| [9] | Y Chen;G D Zhang .[J].Rare Metal Materials and Engineering,1997,26:20. |
| [10] | E G Wolff;B K Min;M H Kural .[J].Journal of Materials Science,1985,20:1141. |
| [11] | F Wu;J Zhu .[J].Compos Sci Techol,1998,58:77. |
| [12] | R Wendt;M Misra .[J].Advances in Optical Structure Systems,1990,1303:554. |
| [13] | I. DUTTA .ROLE OF INTERFACIAL AND MATRIX CREEP DURING THERMAL CYCLING OF CONTINUOUS FIBER REINFORCED METAL--MATRIX COMPOSITES[J].Acta materialia,2000(5):1055-1074. |
| [14] | M Russell-Stevens;R I Todd .[J].Journal of Materials Science,2006,41:6228. |
| [15] | K Li;Z L Pei;J Gong;N L Shi and C Sun .[J].Acta Metallurgica Sinica,2007,43(12):1282. |
| [16] | H F Zhao;C J Xia .[J].Mater Heat Treatment,2007,36(12):37. |
| [17] | E.Pippel;J.Woltersdorf;A.Feldhoff .Nanostructure and mechanical properties of interlayers in fibre reinforced composites[J].Key engineering materials,1997(1):575-582. |
| [18] | F Wu;J Zhu .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,277:143. |
| [19] | A Dorner-reisel;Y Nishida .[J].Analytical Biochemistry,2002,374:635. |
| [20] | K Zhang;Y Q Wang;B L Zhou;Y H Zhou and H L Li .[J].Acta Metall Sin (Eng Lett ),1997,10(05):398. |
| [21] | F Wu;J Zhu .[J].Acta Metallurgica Sinica,1998,34(05):449. |
| [22] | Suraj P rawah .[J].Surface and Interface Analysis,2001,31:629. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%