研究了Bi2O3-MoO3复合掺杂对高磁导率MnZn铁氧体磁特性及微观结构的影响.研究结果表明适当配比的Bi2O3-MoO3复合掺杂有利于促进晶粒均匀致密化,提高样品的起始磁导率.在配方中,当掺杂总量为0.08%(质量)、Bi2O3:MoO3=4:6时,晶粒均匀.材料起始磁导率达到12039,可以用于制备需要具有较大晶粒、高磁导率的材料.
参考文献
| [1] | Murase T .Soft magnetic ferrites[J].Powder Metallurgy Data,2003,2A1:1-7. |
| [2] | Janghorban K;Shokrollahi H .Influence of V2O5 addition on the grain growth and magnetic properties of Mn-Zn high permeability ferrites[J].Journal of Magnetism and Magnetic Materials,2007(1):238-242. |
| [3] | Vladimirtseva L A;Samsonov G V;Gorbatyuk V A .Effect of In2O3 additions on the properties of Mn-Zn ferrite[J].Powder Metallurgy and Metal ceramics,2004,12(08):669-671. |
| [4] | Fan J;Sale F R .The microstructures,magnetic properties and impedance analysis of Mn-Zn ferrites doped with B2O3[J].Journal of the European Ceramic Society,2000,20(16):2743-2751. |
| [5] | Ono K.;Fukunaga S. .Mn-Zn ferrite with MoO/sub 3/ and other oxide additives[J].IEEE Transactions on Magnetics,1999(5):3406-3408. |
| [6] | 冯则坤,李海华,何华辉.掺杂对高磁导率MnZn铁氧体磁特性的影响[J].华中科技大学学报(自然科学版),2004(01):79-81. |
| [7] | 苏桦,张怀武,唐晓莉,向兴元.Bi2O3-MoO3复合掺杂对NiCuZn铁氧体烧结特性和磁性能的影响[J].磁性材料及器件,2003(03):7-8,16. |
| [8] | 聂建华 .高性能MnZn铁氧体材料的制备及机理研究[D].华中科技大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%