304 stainless steel coating was deposited on the Interstitial-Free steel substrate by cold gas dynamic spraying (CGDS). Three-point bending test of the cold sprayed 304 stainless steel coating was tested by SHIMADZU electro-hydraulic servo-controlled fatigue testing machine and the fracture morphology was examined by scanning electron microscopy. The results showed that the fracture behavior of the cold sprayed 304 stainless steel coating was brittleness fracture. The crack in the coating occurred in the interfaces between particles and the crack extended to the internal of the coating with the increase of the load. When the crack has extended to the combination interface between coating and substrate, the crack extended to the two sides. The microstructure and mechanical property of the cold sprayed 304 stainless steel coating have been optimized after heat treatment.
参考文献
| [1] | H.-J. Kim;C.-H. Lee;S.-Y. Hwang .Superhard nano WC-12 percent Co coating by cold spray deposition[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):243-248. |
| [2] | J. Michler;E. Blank .Analysis of coating fracture and substrate plasticity induced by spherical indentors: diamond and diamond-like carbon layers on steel substrates[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2001(1):119-134. |
| [3] | Z.X. Chen;Z.G. Wang;F.H. Yuan;S.J. Zhu.Interfacial fracture behavior of a thermal barrier coating system under four-point bend loading[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008:629-632. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%