研究了铸态Ni3(AlCr)合金及其微晶溅射涂层在900—1000℃下的高温氧化性能,结果表明:铸态Ni3(AlCr)合金在氧化过程中,开始形成以Al2O3为主含有少量NiAl2O4的氧化膜,但氧化膜的粘附性很差,在冷却时很容易剥落,在继续氧化过程中合金表面将形成NiO膜,由于NiO的保护性较差,合金表现出“失稳氧化”行为。而溅射微晶Ni3(AlCr)涂层表面形成的氧化膜与基体粘附良好,冷却过程中未发生剥落。长时间氧化后表面氧化膜只由Al2O3和NiAl2O4组成,未出现NiO,因此溅射微晶化合金的抗氧化
High temperature oxidation resistance of cast Ni3(AlCr)alloy and its sputtered microcrystalline coating was investigated at 900-1000℃in air.The results indicated that the oxide scale formed on the cast alloy was mainly composed of A12O3 at the initial st