提出基于高能球磨法制备磁性磨粒的新工艺。用纯铁粉作为磁介质相、刚玉粉作为磨粒相，采用高能球磨法制备了不同配比、不同球磨时间的磁性磨粒，并用其对45钢外圆表面进行加工试验。结果表明：该工艺制备的磁性磨粒加工效果好；当纯铁粉与刚玉粉按体积比1∶1配比、球磨时间为3 h，所得磁性磨粒的加工效果好，加工6 min时表面粗糙度Ra值可达0.176μm。高能球磨法制备磁性磨粒的工艺过程简单，制备成本较低，加工效果较好，有望进行大规模工业化生产和应用。
A new preparation technology of magnetic abrasives was proposed based on high-energy ball grinding method. Using pure iron powder as magnetic dielectric phase,alumina powder as abrasives,the magnetic abrasives with different ratio, different grinding time were prepared by high energy ball grinding method. Experiments were done for the outer surface of 45 # steel cylindrical workpiece with the prepared abrasives. The results show that finishing effect is good,when the ratio of the pure iron powder and alumina powder is 1∶1,ball grinding time is 3 h. The surface roughness Ra value can reach 0.176μm in 6 min. High energy ball grinding preparation method for magnetic abrasive has advantages of simple process,low cost and good finishing effect,and is hopeful to have large scale industrial application.
参考文献
| [1] | 杨胜强;李文辉;陈红玲.表面光整加工理论与新技术[M].北京:国防工业出版社,2011:49-51,177-187. |
| [2] | Tae-Wan Kim;Jae-Seob Kwak .A Study on Deburring of Magnesium Alloy Plate by Magnetic Abrasive Polishing[J].International Journal of Precision Engineering and Manufacturing,2010(2):189-194. |
| [3] | Li W H;Chen H L;Yang S Q .Research of magnetic induction intensity on magnetic abrasive[J].Key Engineering Materials,2011,455:174-180. |
| [4] | Tae-Wan Kim;Dae-Min Kang;Jae-Seob Kwak .Application of magnetic abrasive polishing to composite materials[J].Journal of Mechanical Science and Technology,2010(5):1029-1034. |
| [5] | Dhirendra K S;Jain V K;Raghuram V .Parametric study of magnetic abrasive finishing forces[J].Journal of Materials Processing Technology,2004,149:22-29. |
| [6] | 高小龙,郑勇,孙帆,王秋红.磁性磨料制备技术的研究进展[J].硬质合金,2010(02):118-123. |
| [7] | 胡斌,芦亚萍.磁性磨粒的制备工艺及其研磨性能研究[J].制造业自动化,2010(04):28-29,130. |
| [8] | 贺美云,单伟忠,郭俊丽.烧结磁性磨料和粘结磁性磨料的对比研究[J].机械工程与自动化,2004(06):61-62,65. |
| [9] | 李浩,李鸿操.高能球磨机技术探索[J].中国新技术新产品,2012(08):106-106. |
| [10] | 陈振华;陈鼎.机械合金化与固液反应球磨[M].北京:化学工业出版社,2006:1-58. |
| [11] | Tsai A P;Tsurui T;Memezawa A .Formation of quasi-crystals through peritectoid reactions from a nonequilibrium cubic phase prepared by mechanical alloying[J].Phil Maglett,1993,67(06):393-398. |
| [12] | Ki Buem Kim;Suk Hwan Kim;Won Tae Kim;Do-Hyang Kim;Kyung-Tae Hong .Structural evolution during heat treatment of mechanically alloyed Al-Cu-Fe-(Si) alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(0):822-829. |
| [13] | 居毅,李宗权.机械合金化的原理及在磁性材料研究中的应用[J].功能材料,2002(01):12-14,18. |
| [14] | 龚慧,卢德宏,蒋业华,周荣,王钊.高能球磨法制备SiC/Al复合粉末的工艺研究[J].特种铸造及有色合金,2011(08):749-753. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%