以聚乙烯醇和壳聚糖为原料,戊二醛为交联剂,透明质酸钠和明胶为添加剂,在醋酸溶液中合成了聚乙烯醇-壳聚糖互穿聚合物,并采用冷冻诱导相分离的方法制备了具有多孔结构的海绵,用红外光谱(FT-IR)和扫描电镜(SEM)方法对其结构进行了表征,研究了影响海绵溶胀性能的多种因素.实验结果表明,当m(PVA-1788):m(CTS)=6:1、m(HANa):m(CTS)=0.4:1、m(戊二醛):m(CTS)=0.283:1、m(GEL):m(CTS)=1:1、C(PVA-1788)=0.97 mol/L时,可制得吸水倍率约为25 g/g成型性能较好的多孔高吸水性海绵.用此海绵对兔耳创面的出血进行止血实验测试,结果表明海绵的止血率为100%,且止血时间缩短、总失血量减小,达到了快速有效的止血效果.
参考文献
| [1] | Choi YS;Hong SR;Lee YM;Song KW;Park MH;Nam YS .Study on gelatin-containing artificial skin: I. Preparation and characteristics of novel gelatin-alginate sponge.[J].Biomaterials,1999(5):409-417. |
| [2] | Ma L;Gao C;Mao Z;Zhou J;Shen J;Hu X;Han C .Collagen/chitosan porous scaffolds with improved biostability for skin tissue engineering.[J].Biomaterials,2003(26):4833-4841. |
| [3] | Kurita K. .Chemistry and application of chitin and chitosan[J].Polymer Degradation and Stability,1998(1/3):117-120. |
| [4] | Xu J.;Gross RA.;Kaplan DL.;Mccarthy SP. .CHITOSAN FILM ACYLATION AND EFFECTS ON BIODEGRADABILITY[J].Macromolecules,1996(10):3436-3440. |
| [5] | 陈欢欢,昝佳,林莹,蒋国强,丁富新.壳聚糖/聚乙烯醇温敏水凝胶的制备及性质研究[J].清华大学学报（自然科学版）,2006(06):843-846. |
| [6] | Jen Ming Yang;Wen Yu Su;Te Lang Leu;Ming Chien Yang .Evaluation of chitosan/PVA blended hydrogel membranes[J].Journal of Membrane Science,2004(1/2):39-51. |
| [7] | 李文波,薛锋,程镕时.化学交联聚乙烯醇（PVA）水凝胶的合成、表征及溶胀特性[J].高分子学报,2006(05):671-675. |
| [8] | 林志丹,张秀菊,宋英,张瑞杰,杨松宵,孙土春,温煦.壳聚糖改性缩醛化聚乙烯醇海绵的性能[J].暨南大学学报（自然科学与医学版）,2007(03):283-287. |
| [9] | Mao JS.;Zhao LG.;Yin YJ.;Yao KD. .Structure and properties of bilayer chitosan-gelatin scaffolds[J].Biomaterials,2003(6):1067-1074. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%