研究了MGH754合金在二次再结晶过程中的组织和结构变化.结果表明,合金在热挤压状态具有细小的等轴晶组织,织构微弱,有利于进行形变加工;二次再结晶后,组织为粗大的柱状晶,且出现强烈的织构随着退火时间延长,{110}<001>和{100}<001>织构含量明显增加,而{110}<111>,{110}<113>和{112}<111>等织构的含量减少.合金棒材的纵向主要为<001>取向.
Microstructure and texture changes during secondary recrystallization of MGH754 alloy were studied. The results show that the as-extruded alloy has a fine equiaxed grain structure and weak texture. After secondary recrystallization annealing, coarse elon-gated grain structure parallel to the extrution dircction and strong texture components existed. The content of { 110} <001 > and { 100} <001> texture components increased, while {110} <111>, {110} <112> and { 112} <111> texture components decreased with the in-creasing of annealing time. The longitudinal direction of MGH754 bar is mainly <001> orientation.