以氟钛酸为成膜剂、磷酸二氢锰为促进剂对热浸镀锌层表面进行钝化处理，获得了氟钛酸转化膜。采用扫描电镜研究了不同处理时间所得转化膜的微观形貌；通过中性盐雾试验、电化学极化和电化学阻抗谱，研究了不同处理时间所得转化膜的耐蚀性。确定了氟钛酸转化膜的制备工艺条件为：H2TiF6(w=60%)5 mL/L，Mn(H2PO4)2·2H2O 15 g/L，pH 2.5，处理时间1 min。与未经处理的热浸镀锌试样相比，经氟钛酸钝化后的试样在中性盐雾试验中出现白锈的时间明显延迟，在5%NaCl溶液中的腐蚀电流密度明显降低，极化电阻和电化学阻抗显著增大。处理时间为1 min时所得转化膜的耐蚀性能最好。
Hot-dip galvanized coating was passivated in a bath consisting of fluorotitanic acid as film-forming agent and manganese dihydrogen phosphate as accelerator. The surface morphologies of the conversion coatings obtained by treating for different time were observed by SEM. The corrosion resistance of the conversion coatings was studied by neutral salt spray (NSS) test, electrochemical polarization method, and electrochemical impedance spectroscopy. The optimal process parameters were determined as follows:H2TiF6 (w = 60%) 5 mL/L, Mn(H2PO4)2·2H2O 15 g/L, pH 2.5, and treatment time 1 min. Compared to the as-prepared hot-dip galvanized coating, the sample passivated with fluorotitanic acid can endure longer time for white rusting in NSS test, and has lower corrosion current density and higher polarization resistance and electrochemical impedance in 5%NaCl solution. The conversion coating obtained by treating for 1 min has the best corrosion resistance.
参考文献
| [1] | 卢锦堂;许乔瑜;孔纲.热浸镀技术与应用[M].北京:机械工业出版社,2006:12-16. |
| [2] | Mirghasem Hosseini,Habib Ashassi-Sorkhabi,Heshmat Allah Yaghobkhani Ghiasvand.Corrosion Protection of Electro-Galvanized Steel by Green Conversion Coatings[J].稀土学报（英文版）,2007(05):537-543. |
| [3] | HAMLAOUI Y;TIFOUTI L;PEDRAZA F .Corrosion behavior of molybdate-phosphate-silicate coatings on galvanized steel[J].Corrosion Science,2009,51(10):2455-2462. |
| [4] | AMADEH A;PAHLEVANI B;HESHMATI-MANESH S .Effects of rare earth metal addition on surface morphology and corrosion resistance of hot-dipped zinc coatings[J].Corrosion Science,2002,44(10):2321-2331. |
| [5] | 许乔瑜,姜瑞.热浸镀锌层表面钛盐转化膜研究[J].电镀与涂饰,2010(03):34-37. |
| [6] | Ramezanzadeh, B.;Attar, M.M. .An evaluation of the corrosion resistance and adhesion properties of an epoxy-nanocomposite on a hot-dip galvanized steel (HDG) treated by different kinds of conversion coatings[J].Surface & Coatings Technology,2011(19):4649-4657. |
| [7] | GRILLI R;ABEL M L;BAKER M A et al.The adsorption of an epoxy acrylate resin on aluminum alloy conversion coatings[J].International Journal of Adhesion and Adhesives,2011,31(07):687-694. |
| [8] | Alyamac, E.;Soucek, M.D. .Acrylate-based fluorinated copolymers for high-solids coatings[J].Progress in Organic Coatings: An International Review Journal,2011(3):213-224. |
| [9] | S.H.Wang,C.S.Liu,F.J.Shan.CORROSION BEHAVIOR OF A ZIRCONIUM-TITANIUM BASED PHOSPHONIC ACID CONVERSION COATING ON AA6061 ALUMINIUM ALLOY[J].金属学报（英文版）,2008(04):269-274. |
| [10] | Deck PD.;Sujdak RJ.;Moon M. .Investigation of fluoacid based conversion coatings on aluminum[J].Progress in Organic Coatings: An International Review Journal,1998(1/4):39-48. |
| [11] | Devicharan Chidambaram;Clive R. Clayton;Gary P. Halada .The role of hexafluorozirconate in the formation of chromate conversion coatings on aluminum alloys[J].Electrochimica Acta,2006(14):2862-2871. |
| [12] | FEDRIZZI L;DEFLORIAN F;BONORA P L .Corrosion behavior of fluotitanate pretreated and painted aluminium sheets[J].Electrochimica Acta,1997,42(06):969-978. |
| [13] | 管勇,刘建国,严川伟.电镀锌钛/锆基无铬化学转化膜的制备与耐蚀性能[J].电化学,2010(04):373-377. |
| [14] | C. Cachet;F. Ganne;S. Joiret;G. Maurin;J. Petitjean;V. Vivier;R. Wiart .EIS investigation of zinc dissolution in aerated sulphate medium - Part II: zinc coatings[J].Electrochimica Acta,2002(21):3409-3422. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%