将含二氮杂萘酮结构、耐高温可溶解的聚芳醚砜(PPBES)与聚芳醚腈酮(PPENK)共混,采用溶液浸渍法制备了玻璃布增强PPBES/PPENK树脂基层压板.讨论了树脂的相容性及树脂配比,研究了共混树脂含量对PPBES/PPENK层压板的室温及150℃弯曲强度、吸水率的影响,对层压板的介电性能、阻燃性能等进行了测试.结果表明:PPBES与PPENK完全相容.当PPBES/PPENK=4/6(质量比),树脂质量分数为35.4％时,层压板的综合性能最佳,且150℃的弯曲强度保持率为95.7％.在1 MHz下,介电常数为3.5,tanδ为0.0037;在DC 500V下,体积电阻率为5.9×1014Ω·cm;阻燃性能达到V-0级.
参考文献
| [1] | 罗道明.改性耐高温(180℃)环氧玻璃纤维布层压板[A].南京,2007:130-136. |
| [2] | 刘锋,许自贵,赵成,李仕文.F级高强度环氧玻璃布层压板的研制[C].第八届全国绝缘材料与绝缘技术学术会议论文集,2002:97-100. |
| [3] | 张晓明;刘雄亚.纤维增强热塑性复合材料及其应用[M].北京:化学工业出版社,2007 |
| [4] | Gao Y;Robetson GP;Guiver MD;Jian XG;Mikhailenko SD;Kaliaguine S .Proton exchange membranes based on sulfonated poly(phthalazinone ether ketone)s/aminated polymer blends[J].Solid state ionics,2005(3/4):409-415. |
| [5] | Sun Y M;Wu T C;Lee H C .Sulfonated poly(phthalazinone ether ketone) for proton exchange membranes in direet methanol fuel cells[J].Journal of Membrane Science,2005,265(01):108-114. |
| [6] | Jian X.G.;Zeng L.;Xu R.X.;Dai Y. .Application of poly(phthalazinone ether sulfone ketone)s to gas membrane separation[J].Journal of Applied Polymer Science,1999(14):2385-2390. |
| [7] | 郑亮.玻璃纤维增强PPBES基复合材料性能[J].工程塑料应用,2012(02):25-27. |
| [8] | 王锦艳,刘程,王守立,王勤祎,蹇锡高.新型覆铜箔玻纤布增强聚芳醚腈酮层压板[J].绝缘材料,2012(04):9-13. |
| [9] | 胡福田,杨卓如.改性聚四氟乙烯覆铜板的制备与性能研究[J].化工新型材料,2007(12):54-56,69. |
| [10] | 温变英.高分子材料与加工[M].北京:中国轻工业出版社,2011 |
| [11] | 郑林,张驰,王洲一,赵培,刘向阳,顾宜.一种改性苯并噁嗪树脂及其玻璃布层压板[J].航空材料学报,2011(01):62-66. |
| [12] | 王明晶 .含二氮杂萘酮联苯结构新型聚芳醚腈的研究[D].大连理工大学,2007. |
| [13] | 郭茂,凌鸿,郑林,顾宜.苯并（噁）嗪和双马来酰亚胺共混树脂性能的研究[J].热固性树脂,2008(01):4-7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%