用水冷铜模吸铸法制备出名义成分(at%,下同)为Sm55-xCexCu15Ni10Al20(x=0,7,10,13,15,20,25)的合金样品.利用X射线衍射仪确定合金的结构,用示差扫描量热计(DSC)研究合金的玻璃转变、晶化和熔化行为.通过过冷液相区宽度△Tx和约化晶化温度Tx/Tm来表征Sm基大块非晶的玻璃形成能力,用Tg和Tx来表征其热稳定性.结果表明,Ce的加入使Sm基块体金属玻璃热稳定性降低,当Ce含量为10 at%时,其玻璃形成能力最强,可以制备出Φ5 mm以上的块体金属玻璃,同时应用Miedema理论和等效电负性差△X讨论了该系列合金的玻璃形成能力.
参考文献
| [1] | Fan G.J.;Loser W. .GLASS-FORMING ABILITY OF RE-Al-TM ALLOYS (RE = Sm, Y; TM = Fe, Co, Cu)[J].Acta materialia,2000(15):3823-3831. |
| [2] | Inoue A;Zhang T;Masumoto T .[J].Materials Transactions,1991,31:425. |
| [3] | Inoue A;Kato A;Zhang T et al.[J].MATERIALS TRANSACTIONS,1991,32(07):609. |
| [4] | Inoue A;Zhang T .[J].Materials Science and Engineering A,1997,226:393. |
| [5] | Inoue A;Zhang T;Kurosaka K et al.[J].Materials Transactions,2001,42(08):1800. |
| [6] | Peker A;Johnson W L .[J].Applied Physics Letters,1993,63:2342. |
| [7] | Conner R D;Dandliker R B;Johnson W L .[J].Acta Materialia,1998,46(17):6089. |
| [8] | Busch R;Bakke E;Johnson W L .[J].Acta Materialia,1998,46(13):4725. |
| [9] | Nishiyama N;Inoue A .[J].Materials Transactions,1997,38(05):464. |
| [10] | 赵作峰,张志,李正,闻平,赵德乾,潘明祥,王万录,汪卫华.新型Pr基大块非晶及其特性研究[J].物理学报,2004(03):850-853. |
| [11] | Inoue A.;Zhang T. .Impact Fracture Energy of Bulk Amorphous Zr_(55)Al_(10)Cu_(30)Ni_5 Alloy[J].Materials transactions,1996(11):1726-1729. |
| [12] | Bakker H.Enthalpies in Alloys-Miedema's Semi-Empirical Model Materials Science Foundations I[M].Switzerland:Trans Tech Publications Ltd,1998:1. |
| [13] | 方守狮;Zhou;周自强;张金龙.[J].Journal of Alloys and Compounds,1999(10):293-295. |
| [14] | 方守狮,肖学山,王庆,夏雷,董远达.Pd基大块金属玻璃过冷液相区与键参数的关系[J].稀有金属材料与工程,2004(11):1132-1135. |
| [15] | 方守狮;肖学山;夏雷 et al.[J].非晶态固体,2003,321:120. |
| [16] | 方守狮;肖学山;夏雷.[J].金属间化合物,2004(12):1069. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%