为了改善纳米ZnO在涂料中的分散性,以钛酸酯偶联剂对其进行改性.研究了丙烯酸聚氨酯清漆、含未改性纳米氧化锌的丙烯酸聚氨酯涂层和添加钛酸酯偶联剂改性后的纳米氧化锌的丙烯酸聚氨酯涂层的防腐蚀性能.结果表明,经过钛酸酯偶联剂改性的纳米ZnO其团聚现象明显消失,与涂料表现出良好的相容性,所得的复合涂层的抗渗透能力明显比清漆和含未改性纳米ZnO复合涂层强.改性纳米ZnO显著提高了丙烯酸聚氨酯涂料的防腐性能.
The nano-Zn0 was modified with titanate coupling agent to improve the dispersibility in coatings. The corrosion resistance of the acrylic polyurethane varnish and the acrylic polyurethane coatings containing nano-ZnObefore and after modification by titanate coupling agent were studied. The results showed that the nano-ZnO after modification with titanate coupling agent has good compatibility with coatings and no agglomerates is observed. The permeability resistance of the composite coating containing modified nano-ZnO is remarkably higher than that of the varnish and the coating containing nano-ZnO without modification. The modified nano-ZnO can remarkably improve the corrosion resistance of the acrylic polyurethane coating.
参考文献
| [1] | MAYER H .The chemistry and properties of silicone resins:network formers (in paints and renders)[J].Pigments and Resin Technology,1998,27(06):364-373. |
| [2] | 周树学,武利民.纳米复合涂料的发展述评[J].涂料工业,2001(09):28-30. |
| [3] | Baer DR.;Burrows PE.;El-Azab AA. .Enhancing coating functionality using nanoscience and nanotechnology[J].Progress in Organic Coatings: An International Review Journal,2003(3/4):342-356. |
| [4] | Y. Du;M.-S. Zhang;J. Hong Y. Shen;Y. Shen;Q. Chen;Z. Yin .Structural and optical properties of nanophase zinc oxide[J].Applied physics, A. Materials science & processing,2003(2):171-176. |
| [5] | 马正先,韩跃新,郑龙熙,刘建彬.纳米氧化锌的应用研究[J].化工进展,2002(01):60-62,69. |
| [6] | 祖庸;雷闫盈;王训 等.纳米ZnO的奇妙用途[J].化工新型材料,1992,27(03):14-16. |
| [7] | 余爱萍;陈雪花;陈忠伟 等.抗紫外纳米ZnO粉体的制备与表面改性[J].上海化工,2001,26(20):13-15. |
| [8] | 张颖怀,许立宁,路民旭,张璞.用电化学阻抗谱（EIS）研究环氧树脂涂层的防腐蚀性能[J].腐蚀与防护,2007(05):227-230,234. |
| [9] | CHEN Y;HONG T;GOPAL M et al.EIS studies of a corrosion inhibitor behavior under multiphase flow conditions[J].Corrosion Science,2000,42(06):979-990. |
| [10] | 刘斌,李瑛,林海潮,曹楚南.丙烯酸聚氨酯涂料防腐蚀性能研究[J].中国腐蚀与防护学报,2003(02):89-91,98. |
| [11] | 张智,熊金平,曹京宜,左禹.不同表面处理等级下有机涂层失效行为的EIS研究[J].新技术新工艺,2008(10):90-93. |
| [12] | 谢德明,胡吉明,童少平.多道环氧涂层在NaCl溶液中的电化学阻抗谱[J].材料研究学报,2004(01):96-101. |
| [13] | 张鉴清 .富锌涂层的电化学阻抗谱特性[J].中国腐蚀与防护学报,1996,16(03):175-180. |
| [14] | 胡吉明,张鉴清,谢德明,曹楚南.环氧涂覆LY12铝合金在NaCl溶液中的阻抗模型[J].物理化学学报,2003(02):144-149. |
| [15] | 魏无际,鲁钢,丁毅,沈民杰.阻垢防蚀涂料的合成及其性能[J].材料保护,2002(01):40-43. |
| [16] | 张而耕,龙康,王志文.纳米复合涂层对碳钢防腐性能的交流阻抗评定[J].腐蚀科学与防护技术,2002(06):337-339. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%