本文研究了真空退火对Nd0.7 Sr0.3 MnO3(NSMO)外延膜的结构和输运性的影响.X-射线衍射(XRD)和电阻率测量结果显示,随着退火温度的升高,NSMO薄膜单胞沿着c-轴方向拉长,电阻率随退火温度的升高而增大,同时金属-绝缘体转变温度(Tp)降低.上述结果归因于真空退火引起的氧缺失导致了Mn3+/Mn4+离子比例的增大及MnO6八面体的畸变.Kroger-vink的缺陷反应式定性的解释了氧缺失与输运性的关系.
参考文献
| [1] | J. Z. Sun;D. W. Abraham;R. A. Rao;C. B. Eom .Thickness-dependent magnetotransport in ultrathin manganite films[J].Applied physics letters,1999(20):3017-3019. |
| [2] | A. Barman;G. Koren .Thickness-dependent transport properties of Nd_(2/3)Sr_(1/3)MnO_(3) thin films[J].Applied physics letters,2000(11):1674-1676. |
| [3] | M. Ziese;H. C. Semmelhack;K. H. Han;S. P. Sena;H. J. Blythe .Thickness dependent magnetic and magnetotransport properties of strain-relaxed La_(0.7)Ca_(0.3)MnO_(3) films[J].Journal of Applied Physics,2002(12):9930-9936. |
| [4] | 金绍维,LI Jin-guang,李金光,单会会,吴文彬,周先意.（La0.6 Nd0.4）0.7Sr0.3 MnO3薄膜的厚度依赖的结构与输运性[J].低温物理学报,2008(02):120-124. |
| [5] | J. R. Sun;C. F. Yeung;K. Zhao .Strain-dependent vacuum annealing effects in La_(0.67)Ca_(0.33)MnO_(3-δ) films[J].Applied physics letters,2000(9):1164-1166. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%