以固体硅胶为硅源考察了六亚甲基亚胺(HMI)和环己胺(CHA)二元胺模板剂对分子筛合成产物的影响. XRD测试结果表明,当晶化温度为160 ℃,晶化时间为84 h, SiO2/Al2O3摩尔比为30, Na2O∶H2O∶(HMI+CHA)∶SiO2摩尔比为0.11∶45∶0.35∶1时,即使HMI仅占二元胺模板剂的25%(摩尔分数),所得分子筛仍为MCM-22; 其它条件相同时,以单纯CHA为模板剂得到的是ZSM-35分子筛. 用 13C MAS NMR研究了HMI和CHA的状态,结果表明在单一HMI合成体系中,HMI既起MCM-22结构导向作用,又经质子化后起稳定骨架的作用; 而在HMI和CHA二元胺体系中,HMI主要起结构导向作用,CHA则填充在MCM-22层间十元环中稳定骨架.
参考文献
| [1] | Leonowicz M E;Lawton J A;Lawton S L;Rubin M K .[J].Science,1994,264(5167):1910. |
| [2] | Rubin M K;Chu P .[P].US 4954325,1990. |
| [3] | Camblor M A;Corell C;Corma A;Diaz-Cabanas M-J,Nicolopoulos S,Gonzalez-Calbet J M,Vallet-Regi M .[J].Chemistry of Materials,1996,8(10):2415. |
| [4] | Zones SI.;Hwang SJ. .Synthesis of high silica zeolites using a mixed quaternary ammonium cation, amine approach: Discovery of zeolite SSZ-47[J].Chemistry of Materials,2002(1):313-320. |
| [5] | Güray I;Warzywoda J;Bac N;Sacco A .[J].Microporous and Mesoporous Materials,1999,31(03):241. |
| [6] | Aiello R;Crea F;Testa F;Demortier G,Lentz P,Wiame M,Nagy J B .[J].Microporous and Mesoporous Materials,2000,35-36:585. |
| [7] | Cheng M J;Tan D L;Liu X M;Han X W,Bao X H,Lin L W .[J].Microporous and Mesoporous Materials,2001,42(2-3):307. |
| [8] | 谢素娟,王清遐,徐龙伢,陈巍,白杰,林励吾.MCM-22型分子筛的合成及其用于生产异丙苯的催化性能[J].催化学报,1999(06):583-584. |
| [9] | Bai J.;Liu SL.;Xie SJ.;Xu LY.;Lin LW. .Shape selectivity in methane dehydroaromatization over Mo/MCM-22 catalysts during a lifetime experiment[J].Catalysis Letters,2003(3/4):123-130. |
| [10] | 谢素娟,彭建彪,徐龙伢,吴治华,王清遐.以环己胺为模板剂的ZSM-35分子筛的合成及其催化性能[J].催化学报,2003(07):531-534. |
| [11] | 谢素娟,王清遐,徐龙伢,吴志华.ZSM-35分子筛的合成及其在1-己烯骨架异构化反应中的应用[J].催化学报,2000(04):297-298. |
| [12] | Rollmann L D;Schlenker J L;Lawton S L;Kennedy C L,Kennedy G J,Doren D J .[J].Journal of Physical Chemistry B,1999,103(34):7175. |
| [13] | Guth J L;Caullet P .[J].Journal of Chim Phys-Chem Biol,1986,83(03):155. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%