SG45钢是在45号钢基础上开发的1种新型的非调质钢,通过对成品棒材进行取样,分析了SG45的化学成分,在光学显微镜及扫描电镜下研究了不同状态下酸浸后的金相样品,研究了钢材组织及夹杂物的分布情况,并对试样进行了拉伸、冲击试验以分析其不同状态下的力学性能。比较了不同状态下SG45钢和45号钢的组织及力学性能,SG45钢作为1种替代性非调质钢,其抗拉强度为472MPa、硬度为230HBW、冲击值为45J、伸长率为36.5%。
As a new kind of non-quenched and tempered steel,SG45 steel is recently developed on the basis of 45 steel.Based on the samples of finished product bar,this article analyzes the chemical composition of SG45,its structure and inclusions distribution for metallographic samples in different state after acid erosion by optical microscopy and scanning electron microscope.In addition,tensile test and impact test which are used to analyze its mechanical properties in different state are also made.As a new alternative non-quenched and tempered steel,its strength（Rm 472 MPa）,hardness（230 HBW）,impact value（45 J） and elongation（A 36.5 %）are all superior to 45 steel,and all the indexes can meet the requirements of customers.
参考文献
| [1] | 戴观文,梁玫,李强,刘宪明,邸俊真,陈连胜.非调质钢SG45的研究及工艺探讨[J].河北冶金,2004(06):21-24,30. |
| [2] | 邱朋军 .非调质钢锻件控锻-控冷技术研究[D].北京科技大学,2009. |
| [3] | 李文涛,吴益文,华沂,蒋海宁,胥成民,吉静.重复加热对调质态45纲组织和性能的影响[J].热处理,2010(02):66-69. |
| [4] | 周红岩.低温轧制对Φ50mm45钢显微组织的影响[J].河北冶金,2010(02):15-18. |
| [5] | 庞永钢;陈煜;王玉钢 等.电磁搅拌对小方坯连铸生产45号钢组织和成分偏析的影响[J].河南冶金,2007,15(05):11. |
| [6] | 魏振卿,柯晓涛,陆建生.对微量钒处理45钢的组织和力学性能的研究[J].金属世界,2010(01):31-33,30. |
| [7] | 陈涛.高温愈合处理对45钢力学性能的影响[J].材料热处理技术,2008(07):28. |
| [8] | 程慧静,王福明,李长荣,谭燕萍,王建军.砷对45钢组织及力学性能的影响[J].金属热处理,2010(02):33-38. |
| [9] | 贺睿;李雷;郭世敬.亚温淬火温度45钢组织性能的影响[J].材料热处理技术,2010(01):141. |
| [10] | 项程云.合金结构钢[M].北京:冶金工业出版社,1999 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%