对化学镀法制备铜包钼的钼铜复合粉体的烧结致密化特点进行了研究,讨论了化学镀法制备钼铜复合粉的成形性,分析了化学镀铜钼粉的预处理、烧结温度、保温时间及复压复烧工艺对致密化的影响.结果表明,化学镀法制备钼铜复合粉成形性好,生坯相对密度可达到87%.在优化各影响因素的情况下,Mo/28Cu采用常规粉末冶金工艺得到了相对密度达97%的钼铜复合材料,钼铜复合材料具有典型的网络状结构,复合材料内部基本无孔洞,铜相分布均匀.
参考文献
| [1] | 刘正春,王志法,姜国圣.金属基电子封装材料进展[J].兵器材料科学与工程,2001(02):49-53. |
| [2] | 牟科强,邝用庚.Mo-Cu材料的性能和应用[J].金属功能材料,2002(03):26-29. |
| [3] | M. H. Maneshian;A. Simchi;Z. Razavi Hesabi .Structural changes during synthesizing of nanostructured W-20 wt% Cu composite powder by mechanical alloying[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):86-93. |
| [4] | 吉洪亮,堵永国,张为军.W/Cu、Mo/Cu合金的致密化技术[J].电工材料,2001(03):13-17. |
| [5] | Gusmano G.;Polini R.;Magistris P.;Marcheselli G.;Bianco A. .Chemical synthesis and sintering behaviour of highly dispersed W/Cu composite powders[J].Journal of Materials Science,2001(4):901-907. |
| [6] | Raghu T.;Ramakrishnan P.;Mohan TRR.;Sundaresan R. .Synthesis of nanocrystalline copper-tungsten alloys by mechanical alloying[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(0):438-441. |
| [7] | 杨文彬,张冰杰,沈丹,周元林,戴亚堂,胡小平,李鸿波,雷刚.空心玻璃微珠表面化学镀Ni-P合金磁性涂层的研究[J].功能材料,2007(11):1856-1858. |
| [8] | 黄伯云.粉末冶金原理[M].北京:冶金工业出版社,1982 |
| [9] | 王文芳.石墨表面镀铜对石墨-铜复合材料强度影响的研究[J].热加工工艺,1999(06):28. |
| [10] | 蔡一湘;刘伯武 .钨铜复合材料致密化问题和方法[J].粉末冶金工业,1997,17(02):138-144. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%