裂纹既是复合材料梁构件的主要损伤类型之一,也是构件失效的主要原因之一.材料产生裂纹时,由于内部能量分布的变化,对外显现的动态特性会发生明显变化.对健康构件试样和裂纹损伤试样进行了大量对比研究,找到了损伤状态下动态特性的特征分布,并以此为依据建立了裂纹损伤的诊断规则.
Crack is one of the chief damages in composite material beams, and it is also one of the chief reasons which results in malfunction. When crack is developed, the inner energy distribution will change, causing the apparent change of the dynamic behaviour. With massive comparative trials to both healthy samples and damaged samples, the characteristic distribution of dynamic behaviour can be obtained, and based on it the diagnosis criteria for crack damage can be established
参考文献
| [1] | 赵鸿汉.环氧基纤维增强复合材料应用面面观[J].玻璃钢/复合材料,2006(02):23. |
| [2] | 肖生祥;樊丁 .环氧树脂与玻璃纤维复合材料的用研究[J].山西建筑,2007,33(01):170. |
| [3] | 欧进萍.重大工程结构智能传感网络与健康监测系统的研究与应用[J].中国科学基金,2005(01):8-12. |
| [4] | 贺跃进,张恒.复合材料层合板裂纹诊断的实验研究[J].玻璃钢/复合材料,2008(02):23-25,34. |
| [5] | 唐桂云,王云飞,吴东辉,李建国.先进复合材料的无损检测[J].纤维复合材料,2006(01):33-36. |
| [6] | Hong M;Chen H R .Dynamic behavior of laminated composite plates with delamination[J].J Shipbuilding Struct Mech,2000,4(06):28. |
| [7] | 王小永,钱华.先进复合材料中的主要缺陷与无损检测技术评价[J].无损探伤,2006(04):1-7. |
| [8] | 胡卫兵,李立洲,闫云聚.复合材料层合梁结构在线损伤检测[J].西安建筑科技大学学报(自然科学版),2002(01):48-52. |
| [9] | Mark Lin;Fu-Kuo Chang .Composite structures with buildin diagnostics[J].Materials Today,1999,2(02):18. |
| [10] | 张小玉 .碳纤维智能层的特性及其场域监测[D].武汉理工大学,2007. |
| [11] | 褚武扬;林实;田中卓.断裂韧性测试[M].北京:科学出版社,1979:17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%